View Patent ↗A method of manufacturing a magnetic recording medium facilitates preventing a film inflation from occurring in an environmental condition range between −40° C. and 80° C. and an 80% relative humidity. The magnetic recording medium includes a plastic substrate and an undercoating layer on the plastic substrate. The undercoating layer is provided with a columnar structure, which prevents water (moisture) between the plastic substrate and the undercoating layer from aggregating and, therefore, the film inflation from occurring.
1. A method of manufacturing a magnetic recording medium comprising a nonmagnetic substrate made of a polymer resin, a magnetic layer above the nonmagnetic substrate, a protection layer above the magnetic layer, and a liquid lubricant layer on the protection layer, the method comprising:
forming an undercoating layer on the nonmagnetic substrate between the nonmagnetic substrate and the magnetic layer under a pressure between approximately 30 mTorr and approximately 80 mTorr; and
forming an intermediate layer on the undercoating layer under a pressure of 60 mTorr or higher.
2. The method according to claim 1 , wherein the undercoating layer comprises a TiW alloy.
3. The method according to claim 1 , wherein the undercoating layer comprises Ru, Re or Os as a component thereof.
4. The method according to claim 1 wherein the intermediate layer formed on the undercoating layer comprises a TiW alloy.
5. The method according to claim 1 , wherein the intermediate layer comprises Ru, Re or Os as a component thereof.
6. A method of manufacturing a magnetic recording medium comprising a nonmagnetic substrate, a magnetic layer above the nonmagnetic substrate, a protection layer above the magnetic layer, and a liquid lubricant layer on the protection layer, the method comprising:
forming an undercoating layer on the nonmagnetic substrate under a pressure between approximately 30 mTorr and approximately 80 mTorr; and
forming an intermediate layer on the undercoating layer under a pressure of 60 mTorr or higher.
7. A method of manufacturing a magnetic recording medium comprising a nonmagnetic substrate, an undercoating layer on the nonmagnetic substrate, a CoCrPt—SiO 2 layer above the undercoating layer, a Ti layer above the CoCrPt—SiO 2 layer, a CN layer above the Ti Layer, and a lubricant layer on the CN layer, the method comprising:
forming an undercoating layer on the nonmagnetic substrate between the nonmagnetic substrate and the CoCrPt—SiO 2 layer under a pressure between approximately 30 mTorr and approximately 80 mTorr; and
forming an intermediate layer on the undercoating layer under a pressure of 60 mTorr or higher.