Dewatering of a paper web in a press section of a papermaking machine
View Patent ↗A press felt for use in the press section of a papermaking machine. The felt is comprised of at least one base fabric to which at least one batt layer is attached by needling or another suitable method. A woven or nonwoven fibrous scrim may be included between the base fabric and the at least one layer of batt material, or between any two or more layers. At least one of the base fabric, the at least one layer of batt material, or the fabric scrim is comprised of polymeric fibers which are blended with fibers whose modulus of elasticity is substantially less than the modulus of elasticity of the polymeric fibers. Press felts manufactured in accordance with the teachings of the invention provide a retarded elastic spring-back in the vertical (or Z) direction of the felt following the mid-nip point in the press section. This retarded elastic spring-back advances the post nip separation position of the felt and the paper web towards the mid-nip point, thus reducing rewetting of the paper sheet. Fibers comprised of regenerated celluosics, such as viscose rayon, have proven effective for use as the low modulus of elasticity component fibers in the press fabrics of the invention.
1. A method of improving dewatering of a paper web in a press section of a papermaking machine, comprising:
forming a press felt with a low elasticity batt material including polymeric staple fibers uniformly blended with low elasticity staple fibers having a modulus of elasticity that is less than 25% of a modulus of elasticity of the polymeric staple fibers, and the fibers at the paper support side (PS) consisting of fibers having a dtex of at least about 1.1;
providing a nip between first and second press rolls in the press section of a papermaking machine, with the press felt extending through the nip;
transferring an embryonic paper to the press felt;
conveying the embryonic paper web into the nip on the press felt; and
advancing a paper web separation point from the press felt to limit rewetting of the paper web after a mid nip point due to retarding an elastic spring back of the press felt after the mid nip point.
2. The method of claim 1 , further comprising:
forming the press felt with at least one PS batt layer comprised of regenerated cellulosic staple fibers.
3. The method of claim 2 , further comprising:
forming the press felt with the at least one PS batt layer comprising a blend of the regenerated cellulosic staple fibers and polymeric staple fibers.
4. The method of claim 3 , further comprising providing the regenerated cellulosic staple fibers having a dtex from at least about 1 to about 44.
5. A press felt for use in a papermaking machine, comprising:
a base fabric layer and a staple fiber batt material layer attached to the base fabric layer, the staple fiber batt material layer includes polymeric stable fibers uniformly blended with low elasticity staple fibers having a modulus of elasticity that is less than 25% of a modulus of elasticity of the polymeric stable fibers, the polymeric staple fibers and the low elasticity staple fibers consisting of fibers having a dtex of at least about 1.1 to about 44.
6. The press felt of claim 5 , wherein the low elasticity staple fibers comprise regenerated cellulosic staple fibers.
7. The press felt according to claim 5 , wherein the polymeric staple fibers and the low elasticity staple fibers have an approximately equal size.
8. The press felt according to claim 5 , wherein the polymeric staple fibers are comprised of nylon.
9. The press felt according to claim 5 , wherein the staple fiber batt material layer is comprised of between 20% to 80% by weight of the low elasticity staple fiber and from 80% to 20% by weight of the polymeric staple fiber.
10. The press felt according to claim 5 , wherein the staple fiber batt material layer is comprised of between 50% to 80% by weight of the low elasticity staple fiber and from 50% to 20% by weight of the polymeric staple fiber.
11. The press felt according to claim 5 , wherein the staple fiber batt material layer is comprised of about 50% by weight of the low elasticity staple fiber and about 50% by weight of the polymeric staple fiber.
12. The press felt according to claim 5 , wherein the staple fiber batt material layer comprises a plurality of layers of staple fiber batt material, the low elasticity staple fibers being located at least on a paper support side of the press felt.