Intumescent coating
A coating composition useful for building materials products, especially roofing surfaces, is provided. The coating composition provides durable exterior protection to surfaces that it applied to, and it has intumescent and reflective properties. The coating composition includes a mixture of a polymeric binder, at least one intumescent agent, a polymeric carrier and a pigment. The pigment is present in the coating composition in amount that is capable of providing a coating that has an initial energy efficiency rating greater than or equal to 0.65 for a low-sloped roof, or an initial energy efficiency greater than or equal to 0.25 for a steep-sloped roof. The coating composition has a solids content from about 30-80% of which 0.5-35 wt. % is the intumescent agent.
1 . A coating composition comprising:
a mixture of a polymeric binder, at least one intumescent agent, a polymeric carrier and an effective amount of a pigment that is capable of providing a coating that has an initial energy efficiency rating greater than or equal to 0.65 for a low-sloped roof, or an initial energy efficiency greater than or equal to 0.25 for a steep-sloped roof, wherein said mixture has a solids content from about 30-80% of which 0.5-35 wt. % is said at least one intumescent agent.
2 . The coating composition of claim 1 wherein the polymeric binder is a thermoplastic polymer or a thermoplastic rubber.
3 . The coating composition of claim 2 wherein the polymeric binder is a thermoplastic polymer selected from the group consisting of acrylic or methacrylic polymers or copolymers, epoxy resins, polyvinyl acetate, and urethane.
4 . The coating composition of claim 2 wherein the polymeric binder is a thermoplastic rubber selected from the group consisting of styrene-butadiene rubbers, styrene-butadiene-styrene rubbers, styrene-ethylene-butadiene-styrene (SEBS) rubbers, styrene isoprene styrene (SIS) rubbers, and styrene butadiene rubbers.
5 . The coating composition of claim 1 wherein the polymeric carrier is water or a hydrocarbon solvent.
6 . The coating composition of claim 1 wherein the pigment comprises titanium dioxide, calcium carbonate, colemanite, aluminum trihydrate (ATH), borate compounds or mixtures thereof.
7 . The coating composition of claim 1 wherein the pigment is titanium dioxide.
8 . The coating composition of claim 1 wherein the polymeric binder and the polymeric carrier form an aqueous polymeric-based emulsion.
9 . The coating composition of claim 1 wherein the polymeric binder and the polymeric carrier form a solvent polymeric-based emulsion.
10 . The coating composition of claim 1 wherein the polymeric binder is present in said mixture in an amount from about 5 to about 60 wt. %.
11 . The coating composition of claim 1 wherein the polymeric carrier is an acrylic polymer that is present in said mixture in an amount from about 30 to about 50 wt.
12 . The coating composition of claim 1 wherein the polymeric carrier is a thermoplastic rubber that is present in said mixture in an amount from about 8 to about 18 wt. %.
13 . The coating composition of claim 1 wherein the pigment is present in said mixture in an amount from about 2 to about 20 wt. %.
14 . The coating composition of claim 1 wherein said at least one intumescent agent comprises expandable graphite particles.
15 . The coating composition of claim 1 further comprising one or more optional components selected from the group consisting of dispersants, defoamers, fillers, solvents, microbiocides, thickening agents, additional fire retardants, pH modifiers, wetting agents, light stabilizers, and adhesion promoters.
16 . A coating comprising:
a cured reaction product of a polymeric binder, at least one intumescent agent, a polymeric carrier and a pigment, said cured reaction product having an initial energy efficiency rating greater than or equal to 0.65 when applied to low-sloped roof, or an initial energy efficiency greater than or equal to 0.25 when applied to a steep-sloped roof.
17 . The coating of claim 16 wherein said at least one intumescent agent is expandable graphite particles.
18 . A roofing product comprising the coating of claim 16 and at least one of a substrate or a material layer of a building materials product.
19 . The roofing product of claim 18 wherein the substrate has surfaces with a slope of 2:12 inches or less.
20 . The roofing product of claim 18 wherein the substrate has surfaces with a slope of greater than 2:12 inches.
21 . The roofing product of claim 18 wherein the substrate comprises composite shingles, clay, concentrate, fiber cement tile, slate, shakes, architectural profiled metal or individual roofing components.