Composition and method of forming aluminum alloy foil
The present invention provides an aluminum alloy foil for fins used in heat exchangers. The aluminum alloy composition consists essentially of about 0.25% to about 0.6% by weight of Si; about 0.15% to about 0.50% by weight of Fe; about 0.20% to about 0.70% by weight of Mn; less than about 0.05% Cu; and less than about 0.05% Mg, with the balance aluminum including unavoidable impurities. The alloy composition may also contain less than 0.10% Zn or 0.50-2.00% Zn. The invention also provides a method for making an aluminum alloy wherein during cold rolling interanneal is carried out at a gauge such that the cold work after internanneal is between about 30-70%.
1 . An aluminum-based alloy consisting essentially of about 0.25% to about 0.60% by weight of Si; about 0.15% to about 0.50% by weight of Fe; about 0.20% to about 0.70% by weight of Mn; less than about 0.05% Cu; and less than about 0.05% Mg, with the balance aluminum including unavoidable impurities.
2 . The alloy of claim 1 , wherein the alloy contains 0.10% by weight of Zn.
3 . The alloy of claim 1 , wherein the alloy contains 0.50-2.00% by weight of Zn.
4 . The alloy of claim 1 , wherein the alloy contains about 0.3-0.5% by weight of silicon.
5 . The alloy of claim 1 , wherein the alloy contains about 0.15-0.35% by weight of iron.
6 . The alloy of claim 1 , wherein the alloy contains about 0.30-0.60% by weight of manganese.
7 . The alloy of claim 1 , wherein the alloy contains about 0.40-0.80% by weight of manganese and iron.
8 . The alloy of claim 1 in the form of a cold rolled sheet, wherein during cold rolling interanneal is carried out at a gauge such that the cold work after interanneal is between 30-70%.
9 . An aluminum foil made by continuously casting an aluminum alloy strip from a molten alloy having a composition in accordance with claim 1 , and cold rolling the continuous cast aluminum strip to a final gauge of between about 0.002-0.008 inches.
10 . A heat exchanger having fins comprising an alloy having a composition in accordance with claim 1 .
11 . A fin for a heat exchanger comprising an alloy having a composition in accordance with claim 1 .
12 - 20 . (Canceled)
21 . An aluminum foil made by continuously casting an aluminum alloy strip from a molten alloy having a composition in accordance with claim 1 , and cold rolling the continuous cast aluminum strip to a final gauge of between about 0.002-0.008 inches, wherein the cold rolling step is carried out at a gauge such that the cold work after cold rolling is between 30% to 70%.
22 . A heat exchanger having fins comprising an alloy made by continuously casting an aluminum alloy strip from a molten alloy having a composition in accordance with claim 1 , and cold rolling the continuous cast aluminum strip to a final gauge of between about 0.002-0.008 inches, wherein the cold rolling step is carried out at a gauge such that the cold work after cold rolling is between 30% to 70%.
23 . A fin for a heat exchanger comprising an alloy made by continuously casting an aluminum alloy strip from a molten alloy having a composition in accordance with claim 1 , and cold rolling the continuous cast aluminum strip to a final gauge of between about 0.002-0.008 inches, wherein the cold rolling step is carried out at a gauge such that the cold work after cold rolling is between 30% to 70%.