UV-absorbing coatings and methods of making the same
View Patent ↗Methods of forming UV-absorbent transparent coatings and transparent substrates coated with the same allow for a relatively lower temperature cross-linkage reaction between a UV-absorbent compound and an epoxy-alkoxysilane. More specifically, UV-absorbent coatings on transparent substrates are formed by prepolymerizing a mixture consisting essentially of a benzophenone, an epoxy alkoxysilane and an organic catalyst at a temperature of between about 40° C. to about 130° C. and for a time sufficient such that between about 30% to about 70% of the epoxy alkoxysilane has been converted to a ring-opened oligomer or polymer. Such prepolymerized mixture may then be hydrolyzed and coated onto the surface of a transparent substrate, and thereafter cured at a temperature of less than about 200° C. for a time sufficient to cross-link the hydrolyzed alkoxysilane with itself and the glass surface. Most preferably, the prepolymerized mixture is hydrolyzed prior to being coated onto the substrate in an acidic alcoholic solution. Preferred for use in the present invention as a UV-absorbent compound is tetrahydroxybenzophenone. The preferred epoxy alkoxysilane is 3-glycidoxypropyl trimethoxysilane. It is especially preferred that prepolymerization be effected in the presence of an organic catalyst, such as triethylamine (TEA).
1. A method of forming an ultraviolet (UV) absorbent coating on a transparent substrate comprising the sequential steps of:
(a) prepolymerizing a mixture consisting of a benzophenone, an epoxy alkoxysilane and a tertiary amine catalyst at an elevated temperature of between about 40° C. to about 130° C. for a time sufficient such that between about 30% to about 70% of the epoxy alkoxysilane moieties are in a ring-opened state;
(b) forming a solution of the prepolymerized mixture in an aqueous acidic alcoholic solution and allowing the prepolymerized mixture to hydrolyze so as to form a hydrolyzed coating material therefrom;
(c) coating a layer of the hydrolyzed coating material onto the surface of a transparent substrate; and thereafter
(d) curing the hydrolyzed coating material of the coating layer at an elevated temperature of less than about 200° C. and for a time sufficient to cross-link the epoxy alkoxysilane.
2. The method of claim 1 , wherein the benzophenone is at least one selected from the group consisting of trihydroxybenzophenones, dihydroxybenzophenones, hydroxybenzophenones, and tetrahydroxybenzophenone.
3. The method of claim 1 , wherein the epoxy alkoxysilane is at least one selected from the group consisting cyclohexylepoxy, cyclohexylepoxyethyl, cyclopentylepoxy, epoxyhexyl trimethoxy silanes, epoxyhexyl triethoxysilanes, glycidylmetheyldimethoxysilane and 3-glycidoxypropyl trimethoxysilane.
4. The method of claim 1 , wherein the benzophenone is tetrahydroxybenzophenone, and the epoxy alkoxysilane is 3-glycidoxypropyl-trimethoxysilane, and wherein step (a) is practiced by prepolymerizing the mixture thereof in the presence of triethylamine (TEA).
5. The method of claim 1 , wherein step (a) is practiced by maintaining the mixture at the elevated temperature by heating for between 2 to 10 hours.
6. The method of claim 1 , wherein the aqueous acidic alcoholic solution comprises n-propanol.
7. The method of claim 1 , wherein the tertiary amine catalyst is triethylamine (TEA) or tributylamine (TBA).