Method for brazing metal components for use in medical equipment, metal assembly produced by the method and endoscope provided with the metal assembly

1. A method for brazing two or more of metal components made of stainless steel for use in medical equipment, in which one component is joined to other component using a brazing material containing Au of which amount is 62.5 wt % or higher, the method comprising:

subjecting the components to a heat treatment at a temperature of 1,050 to 1,200° C. in a hydrogen containing atmosphere or in a vacuum;

thereafter bringing one of the components close to the other component so as to form a gap therebetween; and

supplying the brazing material containing Au of which amount is 62.5 wt % or higher in a molten state into the gap to join the metal components together.

2. The method as claimed in claim 1 , wherein the heat treatment is in a hydrogen containing atmosphere, and a dew point of the hydrogen containing atmosphere is −60° C. or lower.

3. A method for brazing two or more of metal components made of stainless steel for use in medical equipment, at least one of the metal components being a hollow member, in which one component is joined to other component using a brazing material containing Au of which amount is 62.5 wt % or higher, the method comprising:

subjecting the components to a heat treatment at a temperature of 1,050 to 1,200° C. in a hydrogen containing atmosphere or in a vacuum;

thereafter a part of one component is inserted into the other component so as to form a gap therebetween; and

supplying the brazing material containing Au of which amount is 62.5 wt % or higher in a molten state into the gap to join the metal components together.

4. The method as claimed in claim 3 , wherein each of the metal components is a hollow member having an internal cavity, in which the gap is formed by inserting a part of one component into the internal cavity of the other component.

5. The method as claimed in claim 1 , wherein the average width of the gap is in the range of 0.02 to 0.25 mm.

6. The method as claimed in claim 1 , wherein the method further comprises, prior to the supplying the brazing material in a molten state into the gap, temporarily fixing the components by welding a part of the one component to a part of the other component by laser welding.

7. The method as claimed in claim 1 , wherein the method further comprises, prior to supplying the brazing material in a molten state into the gap, applying the brazing material along an opening of the gap, in which the brazing material is molten by heating the brazing material thereby supplying the brazing material in a molten state into the gap.

8. The method as claimed in claim 7 , wherein in the supplying the brazing material in a molten state includes heating at a temperature is in the range of 1,050 to 1,200° C.

9. The method as claimed in claim 1 , wherein the supplying the brazen material in a molten state is performed in a hydrogen containing atmosphere or in a vacuum.

10. The method as claimed in claim 1 , wherein the bringing one of the components close to the other component so as to form a gap therebetween includes bringing the metal components close to each other so that a surface of one metal component faces a surface of the other metal component, and forming at least one protrusion on at least one of the surfaces of the metal components so as to protrude toward the other surface.

11. The method as claimed in claim 10 , wherein the protrusion is formed by overlying welding.

12. The method as claimed in claim 10 , wherein the forming the protrusion is carried out prior to the subjecting the components to a heat treatment.

13. The method as claimed in claim 1 , wherein the brazing material is at least one selected from pure gold, Au—Ni based alloys, Au—Cu based alloys and Au—Ag—Cu based alloys.