Aqueous dispersion, its production method, and its use

1. An aqueous dispersion comprising (A) at least one thermoplastic resin; (B) at least one dispersing agent; and (C) water; wherein the dispersion has a pH of less than 12; wherein the thermoplastic resin comprises a copolymer of propylene with at least one comonomer selected from the group consisting of ethylene, a C 4 -C 20 linear, branched or cyclic diene, and a compound represented by the formula H 2 C═CHR wherein R is a C 1 -C 20 linear, branched or cyclic alkyl group or a C 6 -C 20 aryl group, wherein the copolymer of propylene is a propylene-rich alpha-olefin interpolymer comprising units derived from propylene and at least one comonomer selected from the group consisting of ethylene and C4 to C20 alpha-olefins, having a propylene content of greater than 65 mole percent a weight average molecular weight (Mw) of from about 15,000 to about 200,000, a weight average molecular weight/number average molecular weight ratio (Mw/Mn) of from about 1.5 to about 4, and a heat of fusion of from about 30 to about 80 J/g as determined by DSC.

2. The aqueous dispersion according to claim 1 , wherein the propylene-rich alpha-olefin interpolymer is a propylene ethylene interpolymer.

3. The aqueous dispersion according to claim 2 , wherein the propylene ethylene interpolymer has an ethylene content of about 5% to about 25% by weight.

4. The aqueous dispersion of claim 2 , wherein the propylene ethylene interpolymer is a propylene-ethylene copolymer characterized as having 13 C NMR peaks corresponding to a regio-error at about 14.6 and about 15.7 ppm, the peaks of about equal intensity.

5. An aqueous dispersion comprising (A) at least one thermoplastic resin; (B) at least one dispersing agent; and (C) water; wherein the dispersion has a pH of less than 12, and an average particle size of less than about 5 μm, and wherein the dispersing agent comprises less than about 4 percent by weight of the dispersion based on the weight of the thermoplastic resin, wherein the thermoplastic resin is a propylene-ethylene copolymer (a) characterized as having 13 C NMR peaks corresponding to a regio-error at about 14.6 and about 15.7 ppm, the peaks of about equal intensity, and (b) wherein the ethylene is present in that copolymer in an amount of from about 5% to about 25% (by weight) and propylene is present in that copolymer in an amount of from about 95% to about 75% (by weight).

6. The aqueous dispersion of claim 2 , wherein the propylene ethylene interpolymer is a propylene-ethylene copolymer made using a nonmetallocene, metal-centered, heteroaryl ligand catalyst.

7. The aqueous dispersion according to claim 2 , wherein the propylene-rich interpolymer is characterized as having an isotactic triad (mm) measured by 13 C-NMR of greater than about 0.85.

8. The aqueous dispersion of claim 2 wherein the interpolymer has a flexural modulus, measured in accordance with ASTM D-790-97, of less than about 50 kpsi.

9. The aqueous dispersion of claim 1 wherein the interpolymer has a melting point of less than about 140° C.

10. The aqueous dispersion of claim 2 wherein the interpolymer has a melting point of less than about 90° C.

11. The aqueous dispersion of claim 2 wherein the interpolymer has a heat of fusion of less than about 80 J/g.

12. The aqueous dispersion of claim 2 , wherein the propylene-rich interpolymer is a propylene-ethylene copolymer characterized as having 13 C NMR peaks corresponding to a regio-error at about 14.6 and about 15.7 ppm, the peaks of about equal intensity.

13. The aqueous dispersion of claim 3 , wherein the propylene ethylene interpolymer is a propylene-ethylene copolymer characterized as having 13 C NMR peaks corresponding to a regio-error at about 14.6 and about 15.7 ppm, the peaks of about equal intensity.

14. The aqueous dispersion of claim 3 , wherein the propylene ethylene interpolymer is a propylene-ethylene copolymer made using a nonmetallocene, metal-centered, heteroaryl ligand catalyst.

15. An aqueous dispersion comprising (A) at least one thermoplastic resin; (B) at least one dispersing agent; and (C) water; wherein the dispersion has a pH of less than 12; wherein the thermoplastic resin comprises a copolymer of propylene with at least one comonomer selected from the group consisting of ethylene, a C 4 -C 20 linear, branched or cyclic diene, and a compound represented by the formula H 2 C═CHR wherein R is a C 1 -C 20 linear, branched or cyclic alkyl group or a C 6 -C 20 aryl group, wherein the copolymer of propylene is a propylene-rich alpha-olefin interpolymer comprising 5 to 25% by weight of ethylene content and 95 to 75% by weight of propylene content, the copolymer having:

(a) a melting point of less than 90C;

(b) a relationship of elasticity to 500% tensile modulus such that the elasticity is less than or equal to 0.935M+12, where elasticity is in percent and M is the 500% tensile modulus in MPa; and

(c) a relationship of flexural modulus to 500% tensile modulus such that flexural modulus is less than or equal to 4.2e 0.27M +50, where flexural modulus is in MPa and M is the 500% tensile modulus in MPa.

16. The aqueous dispersion of claim 15 , wherein the propylene ethylene interpolymer is a propylene-ethylene copolymer made using a nonmetallocene, metal-centered, heteroaryl ligand catalyst.

17. The aqueous dispersion according to claim 15 , wherein the propylene-rich interpolymer is characterized as having an isotactic triad (mm) measured by 13 C-NMR of greater than about 0.85.

18. The aqueous dispersion of claim 15 , wherein the interpolymer has a flexural modulus, measured in accordance with ASTM D-790-97, of less than about 50 kpsi.

19. The aqueous dispersion of claim 15 , wherein the interpolymer has a heat of fusion of less than about 80 J/g.

20. The aqueous dispersion of claim 1 , wherein the dispersion has a pH ranging from about 7 to 11.

21. The aqueous dispersion of claim 15 , wherein the dispersion has a pH ranging from about 7 to 11.