View Patent ↗Disclosed is a microporous polyethylene film for a battery separator and a method of producing the same. The microporous polyethylene film comprises a resin mixture, which includes 100 parts by weight of composition containing 20-50 wt % polyethylene with a weight average molecular weight of 5×10 4 -3×10 5 (component I) and 80-50 wt % diluent (component II), 0.1-2 parts by weight of peroxide (component III), and 0.05-0.5 parts by weight of anti-oxidant (component IV). The microporous polyethylene film has a puncture strength of 0.22 N/μm or more and a gas permeability (Darcy's permeability constant) of 1.3×10 −5 Darcy or more. The present invention increases production efficiency of the microporous film, and improves performances and stability of the battery when the microporous polyethylene film is used in a battery separator.
1. A method of producing a microporous polyethylene film without the use of irradiation for the purpose of crosslinking, comprising:
(a) melt-extruding a resin mixture to form a sheet, the resin mixture comprising:
100 parts by weight of composition containing 20-50 wt % polyethylene with a weight average molecular weight of 5×10 4 -3×10 5 (component I) and 80-50 wt % diluent (component II);
0.1-2 parts by weight of peroxide (component III); and
0.05-0.5 parts by weight of anti-oxidant (component IV),
(b) stretching the sheet at a temperature range, where 30-80 wt % of a crystalline portion of the sheet is molten, according to a tenter-type simultaneous stretching manner such that stretching ratios are 3 times or more in machine and transverse directions, respectively and a total stretching ratio is 25-50 times to produce a film; and
(c) extracting the diluent from the film, and heat-setting the resulting film, wherein, the microporous polyethylene film has gels of 50 or less per a thickness of 200 μm and area of 2000 cm 2 , a puncture strength of 0.22 N/μm or more and a gas permeability of 1.3 Darcy or more.
2. The method as set forth in claim 1 , wherein the component I contains 2 wt % or less α-olefin comonomer with 3-8 carbons.
3. The method as set forth in claim 1 , wherein the component II includes a paraffin oil with a kinetic viscosity of 20-200 cSt at 40° C.
4. The method as set forth in claim 1 , wherein the component III is selected from the group consisting of a peroxyester-based compound, a diacyl peroxide-based compound, a dialkyl peroxide-based compound, an alkyl hydroperoxide-based compound, an azo-based compound, and a mixture thereof.
5. The method as set forth in claim 1 , wherein the component IV is selected from the group consisting of a phenol-based compound, an amine-based compound, a phosphite-based compound, a thioester-based compound, and a mixture thereof.
6. The method as set forth in claim 1 , wherein a melt-extrusion temperature is 200-250° C. in the step of (a).