High strength steel pipe for an air bag
View Patent ↗In order to manufacture a steel pipe for an air bag which can cope with increase in the pressure of gas blown into an air bag and decreases in the wall thickness of an accumulator, a steel having a composition, mass %, of: C: 0.05-0.20%, Si: 0.1-1.0%, Mn: 0.20-2.0%, P: at most 0.025%, S: at most 0.010%, Cr: 0.05-1.0%, Al: at most 0.10%, if necessary at least one of Mo: at most 0.50%, Ni: at most 1.5%, Cu: at most 0.5%, V: at most 0.2%, Ti: at most 0.1%, Nb: at most 0.1%, and B: at most 0.005%, and also if necessary, at least one of Ca: at most 0.01%, Mg: at most 0.01%, and REM (rare earth elements): at most 0.01%, and a remainder of Fe and impurities is used to produce a steel pipe, and the pipe is then subjected to cold working to predetermined dimensions, then to heating to a temperature of at least the Ac 1 transformation temperature followed by quenching, and then to tempering at a temperature no higher than the Ac 1 transformation temperature.
1. A steel pipe for an air bag having excellent bursting resistance, characterized in that the pipe has a steel composition, in mass %, of:
C: 0.05-0.14%, Si: 0.1-1.0%, Mn: 0.20-2.0%, P: at most 0.025%, S: at most 0.005%, Cr: 0.05-1.0%, Al: at most 0.10%, Mo: 0-0.50%, Ni: 0-1.5%, B: 0-0.005%, Cu: 0-0.5%, Ti: 0-0.1%, Nb: 0-0.1%, V: 0-0.2%, Ca: 0-0.01%, Mg: 0-0.01%, REM (rare earth elements): 0-0.01%, and a remainder of Fe and impurities, the steel pipe having a quenched and tempered structure, a tensile strength of 900 MPa or higher, a low temperature toughness of vTrs 100 of −40° C. or less, and a bursting resistance such that no crack propagation occurs to either end of the pipe when the pipe is subjected to bursting at −40° C., wherein an L/T ratio of an X-ray integrated intensity ratio of the {110} plane in a plane perpendicular to an axial direction L of the steel pipe to that in a plane perpendicular to a circumferential direction T of the steel pipe is at most 4.
2. An accumulator for an air bag made from a steel pipe for an air bag as set forth in claim 1 .
3. A steel pipe for an air bag having excellent bursting resistance, characterized in that the pipe has a steel composition, in mass %, of:
C: 0.05-0.14%, Si: 0.1-1.0%, Mn: 0.20-2.0%, P: at most 0.025%, S: at most 0.005%, Cr: 0.05-1.0%, Al: at most 0.10%, Mo: 0-0.50%, Ni: 0-1.5%, B: 0-0.005%, Cu: 0-0.5%, Ti: 0-0.1%, Nb: 0-0.1%, V: 0-0.2%, Ca: 0-0.01%, Mg: 0-0.01%, REM (rare earth elements): 0-0.01%, wherein at least one of Ca, Mg, and REM is not less than 0.0003%, and a remainder of Fe and impurities, the steel pipe having a quenched and tempered structure, a tensile strength of 900 MPa or higher, a low temperature toughness of vTrs 100 of −40° C. or less, and a bursting resistance such that no crack propagation occurs to either end of the pipe when the pipe is subjected to bursting at −40° C., wherein an L/T ratio of an X-ray integrated intensity ratio of the {110} plane in a plane perpendicular to an axial direction L of the steel pipe to that in a plane perpendicular to a circumferential direction T of the steel pipe is at most 4.
4. An accumulator for an air bag made from a steel pipe for an air bag as set forth in claim 3 .