Engineered structured release liner and processes for making the same
Highly roughened, precision engraved, patterned surface upon a substrate, preferably a polyolefin coated substrate, and processes for making the same. A chill roll is used to impart an engineered, highly structured surface upon the polyolefin coating of the substrate. The structured polyolefin coated substrates preferably have highly regular patterns, and those patterns may include either quadragravure, trihelical, or other regular, reproducible pattern.
1 . A release liner for use with an adhesive facestock, said release liner having a first side and a second side, the first side of said release liner being imparted with a highly engineered, precision engraved, structured pattern, and the second side of said release liner being relatively smooth, and being placed in face-to-face contact with the adhesive facestock.
2 . The release liner of claim 1 , wherein said patterned surface is made of a helicoidal pattern.
3 . The release liner of claim 1 , wherein said patterned surface is made of a quadragravure pattern.
4 . The release liner of claim 1 , wherein said patterned surface is a regular, reproducible pattern.
5 . The release liner of claim 1 , wherein the density of said patterned surface is approximately 50 to 150 lines per inch.
6 . The release liner of claim 3 , wherein the density of said quadragravure pattern is approximately 50 to 150 lines per inch.
7 . The release liner of claims 5 , wherein the depth of the lines are approximately from 12.7 μm to about 88.9 μm.
8 . The release liner of claim 1 , wherein said substrate is a polyolefin coated paper substrate.
9 . The release liner of claim 8 , wherein said paper substrate has a thickness ranging from about 25.4 μm (1 mil) to about 635 μm (25 mils) and a basis weight ranging from about 20 grams per square meter to about 400 grams per square meter.
10 . The release liner claim 8 , wherein said polyolefin is selected from the group consisting of polyethylene, polypropylene, polymethylpentene, and copolymers, terpolymers and blends thereof.
11 . The substrate of claim 8 , wherein said polyolefin coating has a coating weight ranging from about 3.5 grams per square meter to about 47 grams per square meter.
12 . The substrate of claim 11 , wherein said polyolefin coating has a coating weight ranging from about 16 grams per square meter to about 28 grams per square meter.
13 . A release liner including a highly roughened, precision engraved, patterned surface, comprising:
a structured polyolefin coated substrate comprising a substrate and a polyolefin coating on a surface thereof, said polyolefin coating having an Ra surface finish ranging from about 3.8 μm (150 microinches) to about 10.2 μm (400 microinches) and comprising a structure having an Rz ranging from about 22.9 μm (900 microinches) to about 50.8 μm (2000 microinches); and a release coating on a surface of said substrate opposite said polyolefin coated surface.
14 . A process for making a highly roughened, precision engraved, patterned surface upon a substrate, comprising the steps of:
applying a molten polyolefin extrudate onto a surface of a substrate to form a polyolefin coated substrate; and
directing said polyolefin coated substrate through the nip of cooperating rolls, one of said rolls comprising a structure having an average depth ranging from about 12.7 μm (0.5 mil) to about 88.9 μm (3.5 mil) and an Ra surface finish of about 5.1 μm (200 microinches) to about 15.2 μm (600 microinches), under conditions sufficient to impart to a surface of said polyolefin coating a structure having an average height corresponding to the depth of said pockets and a surface finish corresponding to the Ra surface finish of said roll.