Method of manufacture and treatment of wood with injectable particulate iron oxide
A wood preservative includes injectable particles comprising one or more sparingly soluble iron salts. The iron-based particles are sufficiently insoluble so as to not be easily removed by leaching but are sufficiently soluble to exhibit toxicity to primary organisms primarily responsible for the decay of the wood. Wood or a wood product may be impregnated with iron-based particles of the invention.
1 . A wood preservative composition comprising injectable particles of sparingly soluble iron salts, wherein the particle size distribution of the sparingly soluble iron salts is such that the d 98 is about 0.7 microns or less, and the d 99.5 is about 1.5 microns or less.
2 . The wood preservative composition of claim 1 , further comprising a soluble copper complex.
3 . The wood preservative composition of claim 2 , wherein the copper complex is a copper-amine complex, an ammoniacal copper, or copper monoethanolamine carbonate.
4 . The wood preservative composition of claim 1 , further comprising injectable particles of sparingly soluble copper salts.
5 . The wood preservative composition of claim 4 , wherein the sparingly soluble copper salt comprises copper hydroxide, basic copper carbonate, basic copper sulfate, basic copper chloride, basic copper phosphate, basic copper borate, or basic copper phosphosulfate.
6 . The wood preservative composition of claim 1 , further comprising injectable particles of sparingly soluble zinc salts.
7 . The wood preservative composition of claim 6 , wherein the zinc salt is zinc oxide, basic zinc carbonate, zinc hydroxide, or zinc phosphate.
8 . The wood preservative composition of claim 1 , further comprising an injectable suspension of a milled, solid, substantially insoluble organic biocide.
9 . The wood preservative composition of claim 8 , wherein the solid, substantially insoluble organic biocide comprises a triazole, a quaternary ammonium compound, or a carbamide.
10 . The wood preservative composition of claim 1 , wherein the particles comprise an iron oxide.
11 . A wood preservative composition comprising iron oxide particles, wherein the particle size distribution of the iron oxide particles is such that the d 98 is about 0.7 microns or less, and the d 99.5 is about 1.5 microns or less.
12 . The wood preservative of claim 11 , wherein the particle size distribution of the iron oxide particles is such that d 50 is between about 25 nanometers and about 500 nanometers.
13 . The wood preservative of claim 11 , wherein the particle size distribution of the iron oxide particles is such that d 50 is between about 50 nanometers and about 250 nanometers.
14 . The wood preservative of claim 11 , wherein the iron oxide particles are wet milled with a milling media comprising beads having a diameter between about 0.1 mm and about 0.8 mm, and having a density greater than 3 g/cc.
15 . The wood preservative of claim 11 , wherein the injectable particles comprise a substantially insoluble organic biocide disposed on the surface thereof.
16 . The wood preservative of claim 15 , wherein the organic biocide further comprises a surface-active agent.
17 . The wood preservative of claim 11 , further comprising a scale precipitation inhibitor.
18 . The wood preservative of claim 17 , wherein the scale precipitation inhibitor is an organophosphonate.
19 . A wood preservative composition comprising:
a liquid carrier; and
injectable solid iron oxide particlulates coated with an organic biocide.
20 . The wood preservative of claim 19 , further comprising injectable particles of sparingly soluble copper salts.
21 . The wood preservative of claim 19 , wherein the liquid carrier is substantially free of amines.
22 . A method of preserving wood comprising:
contacting wood with a wood preservative composition comprising an aqueous solution of injectable particles of sparingly soluble copper salts and injectable particles of sparingly soluble iron salts.
23 . The method of claim 22 , wherein the sparingly soluble iron salts comprise iron oxide.
24 . The method of claim 22 , wherein the composition further comprises at least one injectable solid organic compound.