Method for forming fire combustion modified batt
View Patent ↗The present invention relates to a method for forming a fire combustion modified batt. The method comprises the step of forming a blend of nonwoven and oxidized polyacrylonitrile fibers into a web. The oxidized polyacrylonitrile fibers are fire resistant and when blended with nonwoven fibers are relatively easily processed into a batt. A second blend of nonwoven fibers can be formed into a web and layered with the oxidized polyacrylonitrile fiber web to form the batt. The fibers are bonded together with heat, resin or other bonding material and are compressed and cooled. The fire combustion modified batt is useful as fire barriers and fillers in bedding, upholstery and vehicle and aircraft seats, as insulators for apparel, appliances, walls and ducting, as barriers to separate control systems from a heat source, and as components in fire safety gear such as race driver suits and oven and welding mitts.
1. A method for forming a fire combustion modified high-loft fiber batt suitable for use as a fire barrier layer in products requiring loft, compressibility and/or resilience, comprising:
forming a generally homogeneous blend consisting of about 42.5 volume percent to about 45 volume percent oxidized polyacrylonitrile fibers, about 42.5 volume percent to about 45 volume percent polyester carrier fibers and about 10 volume percent to about 15 volume percent polyester binder fibers, said polyester binder fibers having a relatively low melting temperature and said polyester carrier fibers having a relatively high melting temperature;
forming said blend of fibers into a web;
compressing said web to form a batt;
heating said batt at a temperature at or above the melting temperature of said polyester binder fibers and below the melting temperature of said polyester carrier fibers; and
forming a fire combustion modified high-loft fiber batt having a ratio of weight in ounces per square foot to thickness in inches of less than about 2:1 while cooling said batt while compressed to fuse said polyester binder fibers to each other and to said polyester carrier fibers and said oxidized polyacrylonitrile fibers;
said fire combustion modified high-loft fiber batt suitable for use as a fire barrier layer in products requiring loft, compressibility and/or resilience.
2. Products using the fire combustion modified high-loft fiber batt of claim 1 as a fire barrier layer thereof, wherein said products are selected from the group consisting of bedding, upholstery, furniture and seats.
3. Mattresses using the fire combustion modified high-loft fiber batt of claim 1 as a fire barrier layer thereof.
4. A fire combustion modified high-loft fiber batt suitable for use as a fire barrier layer in products requiring loft, compressibility and/or resilience, comprising:
a web having a ratio of weight in ounces per square foot to thickness in inches of less than about 2:1, said web formed from a generally homogeneous blend consisting of (a) between about 42.5 volume percent and about 45 volume percent oxidized polyacrylonitrile, (b) between about 42.5 volume percent and about 45 volume percent polyester carrier fibers and (c) between about 10 volume percent and about 15 volume percent polyester binder, said polyester binder fibers having a low melting temperature relative to said polyester carrier fibers and said polyester carrier fibers having a high melting temperature relative to said polyester binder fibers, said polyester binder fibers being heat-fused to fuse said polyester binder fibers to said oxidized polyacrylonitrile fibers, to said polyester carrier fibers and to other polyester binder fibers.
5. Products using the fire combustion modified high-loft fiber batt of claim 4 as a fire barrier layer thereof, wherein said products are selected from the group consisting of bedding, upholstery, furniture and seats.
6. Mattresses using the fire combustion modified high-loft fiber batt of claim 4 as a fire barrier layer thereof.