View Patent ↗The present invention relates to inner coatings of metal food containers and packaging and to a process for their production. The coatings are applied to the inside of at least a portion of the surface area of containers that are in direct contact with foods or other consumable products and subsequently cured. The coatings include a) at least one polyisocyanate containing an average of at least two NCO groups per molecule, at least 95% of the NCO groups being blocked with a blocking agent, and b) at least one polyhydroxyl compound containing an average of at least two hydroxyl groups per molecule that react with NCO groups.
1. A method of coating the inside of at least a portion of the surface area of containers that are in direct contact with foods or other consumable products comprising
applying a coating composition comprising
a component (a) at least one polyisocyanate containing an average of at least two NCO groups per molecule, at least 95% of the NCO groups being blocked with a blocking agent, and
a component (b) at least one polyhydroxyl compound containing an average of at least two hydroxyl groups per molecule that react with NCO groups, and
curing the coating composition.
2. The method according to claim 1 , wherein polyisocyanates containing isocyanurate and/or iminooxadiazinedione groups are used as component (a).
3. The method according to claim 1 , wherein polyisocyanates based on 1,6-hexane diisocyanate and/or isophorone diisocyanate and/or 4,4′-diisocyanatodicyclohexylmethane are used as component (a).
4. The method according to claim 1 , wherein polyisocyanates based on isophorone diisocyanate are used as component (a).
5. The method according to claim 1 , wherein the isocyanate groups present in component (a) are blocked with lactams, oximes, phenols, alkyl hydroxybenzoates, pyrazoles and/or secondary aliphatic amines.
6. The method according to claim 1 , wherein the isocyanate groups present in component (a) are blocked with ε-caprolactam.
7. The method according to claim 1 , wherein the polyhydroxyl compounds present in component (b) have a content of OH groups of 0.5 to 30 wt. %.
8. The method according to claim 1 , wherein the polyhydroxyl compounds present in component (b) have a molecular weight of between 400 and 10,000.
9. The method according to claim 1 , wherein the polyhydroxyl compounds present in component (b) contain polyesters.
10. The method according to claim 1 , wherein the coating is cured at temperatures of between 100 and 400° C.
11. The method according to claim 10 , wherein the coating is cured at temperatures of between 190 and 230° C.
12. The method according to claim 1 , wherein the coating composition contains an organic solvent.
13. The method according to claim 1 , wherein the coating composition contains a catalyst.
14. The method according to claim 1 , wherein the coating composition further comprises c) one or more additional ingredients selected from the group consisting of plasticizers, flow control agents, pigments, fillers and catalysts for accelerating the curing reaction.