Recyclable repulpable coated paper stock
View Patent ↗A coated paper stock having high moisture vapor barrier characteristics and ingredient compatible with recycling and repulping is disclosed comprising a substrate coated on at least one surface with a subcoat. The subcoat comprises a hydrolyzed amphoteric vegetable protein at at least 11 weight percent based on weight of the subcoat. A top coat is coated over said subcoat. The top coat consists essentially of a water-based dispersion of a film forming vinyl addition polymer, conjugated diene polymer or copolymer of either polymer, such as acrylic polymers, acrylic copolymers, polyvinyl acetate, polyvinyl alcohol, styrene acrylate copolymers, styrene butadiene copolymers, polyvinylidene chloride and polyvinylidene chloride copolymers. The top coat is substantially free of mineral pigments that interfere with the moisture vapor barrier characteristics. The vegetable protein is preferably a hydrolyzed amphoteric soybean protein with an average molecular weight less than 400,000 Daltons.
1. A recyclable coated paper stock having high moisture vapor barrier characteristics comprising:
a substrate coated on at least one surface with a subcoat, said subcoat comprising a hydrolyzed amphoteric vegetable protein from about 11 to 100 weight percent based on weight of the subcoat;
a top coat over said subcoat, said top coat being substantially free of mineral pigment and comprising a water based dispersion of a film forming vinyl addition polymer, conjugated diene polymer or copolymer of either polymer.
2. The coated paper stock according to claim 1 further including a clay, pigment, or mineral filler in the subcoat.
3. The coated paper stock according to claim 1 further including a wax in at least one of the top coat or subcoat.
4. The coated paper stock according to claim 1 wherein said subcoat is in the range of from 0.5 to 30 pounds per 3300 square feet of the substrate.
5. The coated paper stock according to claim 1 wherein the vegetable protein is at least 14 weight percent based on weight of the subcoat.
6. The coated paper stock according to claim 1 wherein said substrate is a cellulose based material.
7. The coated paper stock according to claim 6 wherein said substrate is paper, paperboard, or fiberboard.
8. The coated paper stock according to claim 1 wherein said top coat is in the range of from 0.5 to 30 pounds per 3300 square feet of the substrate.
9. The coated paper stock according to claim 1 wherein the top coat comprises a polymer selected from the group consisting of acrylic polymers, acrylic copolymers, polyvinyl acetate, polyvinyl alcohol, styrene acrylate copolymers, styrene butadiene copolymers, polyvinylidene chloride, and polyvinylidene chloride copolymers.
10. The coated paper stock according to claim 1 wherein the top coat is polyvinylidene chloride.
11. The coated paper stock according to claim 10 wherein the top coat includes in addition styrene acrylate.
12. The coated paper stock according to claim 11 wherein the top coat includes in addition calcium stearate.
13. The coated paper stock according to claim 1 wherein the coated paper stock has an MVTR of less than 7.
14. A recyclable coated paper stock having high moisture vapor barrier characteristics comprising:
a substrate on at least one surface with a subcoat, said subcoat comprising a hydrolyzed amphoteric soybean protein with an average molecular weight of less than 400,000 Daltons, at at least 11 weight percent based on weight of the subcoat;
a top coat over said subcoat, said top coat consisting essentially of a water based dispersion of a film forming vinyl addition polymer, conjugated diene polymer or copolymer of either polymer.
15. The coated paper stock according to claim 14 further including a clay, pigment, or mineral filler in the subcoat.
16. The coated paper stock according to claim 14 further including a wax in at least one of the top coat or subcoat.
17. The coated paper stock according to claim 13 wherein said subcoat is in the range of from 0.5 to 30 pounds per 3300 square feet of the substrate.
18. The coated paper stock according to claim 14 wherein said substrate is a cellulose based material.
19. The coated paper stock according to claim 18 wherein said substrate is paper, paperboard, or fiberboard.
20. The coated paper stock according to claim 14 wherein said top coat is in the range of from 0.5 to 30 pounds per 3300 square feet of the substrate.
21. The coated paper stock according to claim 14 wherein the soybean protein is at least 14 weight percent based on weight of the subcoat.
22. The coated paper stock according to claim 14 wherein the soybean protein is of less than 200,000 Daltons.
23. The coated paper stock according to claim 14 wherein the top coat comprises a polymer selected from the group consisting of acrylic polymers, acrylic copolymers, polyvinyl acetate, polyvinyl alcohol, polyethylene, styrene acrylate copolymers, styrene butadiene copolymers, polyvinylidene chloride, and polyvinylidene chloride copolymers.
24. The coated paper stock according to claim 14 wherein the top coat is polyvinylidene chloride.
25. The coated paper stock according to claim 24 wherein the top coat includes in addition styrene acrylate.
26. The coated paper stock according to claim 25 wherein the top coat includes in addition calcium stearate.
27. The coated paper stock according to claim 14 wherein the coated paper stock has an MVTR of less than 7.
28. A method for manufacturing a recyclable coated paper stock having high moisture vapor barrier characteristics comprising:
providing a substrate;
applying a subcoat to at least one surface of said substrate, said subcoat comprising a hydrolyzed amphoteric vegetable protein from about 11 to 100 weight percent based on weight of the subcoat;
applying a top coat over said subcoat, said top coat being substantially free of mineral pigment and comprising a water based dispersion of a film forming vinyl addition polymer, conjugated diene polymer or copolymer of either polymer;
drying said top coat to form the coated paper stock having high moisture vapor barrier characteristics.