Yarn with heat-activated binder material and process of making
View Patent ↗Yarn suitable for tufting comprises a base fiber ring spun or wrap spun with a second fiber at least partially comprising a heat-activated adhesive material such that the yarn includes from 0.1 to 12, preferably 0.25 to 10, weight percent adhesive material having a melting point within the range of 105° to 190° C., more preferably 165° to 190° C. A preferred base fiber is a synthetic staple fiber bundle. A preferred wrapping or insert fiber comprises copolyamide material, including ternary copolyamides of the 6/66/12 type. When the yarn is twist set by conventional processes and then tufted into carpet, the resulting carpet displays enhanced wear and appearance properties.
1. A process for producing a plied yarn suitable for tufting, said process comprising the steps of:
a. forming a bundle of fiber;
b. ring spinning the bundle of fiber into a ring spun yarn;
c. twisting at least two ring spun yarns with at least one second fiber to form a plied yarn, said second fiber(s) comprising a heat-activated binder material having a melting point of about 105 to 190° C. under ambient conditions, said plied yarn comprising 0.1 to 12 weight percent of the binder material;
d. heating the plied yarn sufficiently to melt the binder material; followed by
e. cooling the plied yarn to solidify the binder material.
2. The process of claim 1 , wherein the bundle of fiber is formed by spinning staple fiber.
3. The process of claim 1 wherein said heating step occurs during twist setting of the plied yarn.
4. The process of claim 1 wherein the bundle of fiber is formed by spinning staple fiber.
5. A plied yarn made in accordance with the process of claim 1 .
6. The process of claim 1 wherein the twisting is ply twisting and wherein the ring spun yarns are wound with the second fiber(s) to form an assembly wound package to provide the feed yarns for ply twisting.
7. The process of claim 6 wherein said heating step occurs during twist setting of the plied yarn.
8. The process of claim 6 wherein the bundle of fiber is formed by spinning staple fiber.
9. A plied yarn produced in accordance with the process of claim 6 .
10. The process of claim 1 wherein the fiber is nylon-6 having melt point range of 215 to 225° C.
11. The process of claim 1 wherein the bundle consisting essentially of a first base fiber is selected from the group consisting of a sliver and a bundle of continuous filaments.
12. The process of claim 1 wherein said fiber is a polyamide selected from the group consisting of nylon-6 and nylon-6,6.
13. The process of claim 1 wherein said second fiber comprises a copolyamide.
14. The process of claim 1 wherein said second fiber comprises a copolyamide of nylon 6/nylon 6,6 or nylon 6/nylon 6,6/nylon 12.
15. The process of claim 1 wherein said fiber is a polyamide and said second fiber comprises a copolyamide.
16. The process of claim 1 wherein said fiber is a polyamide selected from the group consisting of nylon-6 and nylon-6,6 and wherein said second fiber comprises a copolyamide of nylon 6/nylon 6,6 or nylon 6/nylon 6,6/nylon 12.
17. The process of claim 1 wherein said second fiber(s) comprises a heat-activated binder material having a melting point of about 165 to 190° C.
18. The process of claim 1 wherein said plied yarn comprises 0.1 to 12 weight percent of the binder material.
19. The process of claim 1 wherein said plied yarn comprises 0.25 to 10 weight percent of the binder material.
20. The process of claim 1 wherein said plied yarn comprises 0.5 to 8 weight percent of the binder material.