Method of producing a microporous polyolefin membrane
View Patent ↗A method for producing a microporous polyolefin membrane formed by fine fibrils, the membrane comprising (A) a polyolefin having a weight-average molecular weight of 5×10 5 or more or (B) a composition containing Component (A), connected to each other, and having micropores of 0.05 to 5 μm in average pore size and crystal lamellas of Component (A) or (B) being in a specific alignment state. The method includes extruding a solution of Component (A) or (B) in a solvent into a gel-like formed article; thermally setting the article, with or without stretching, at least at the crystal dispersion temperature of Component (A) or (B), but at melting point of Component (A) or (B) plus 30° C. or lower; and removing the solvent.
1. A method of producing a microporous polyolefin membrane, comprising the steps of
extruding a solution comprising
10 to 50 weight % of a polyolefin (A) having a weight-average molecular weight of 5×10 5 or more, or a composition (B) containing polyolefin (A) and
50 to 90 weight % of a solvent
into a gel-like formed article; and then
thermally setting the article, with or without stretching, at least at the crystal dispersion temperature of said polyolefin (A) or said composition (B), but at the melting point of said polyolefin (A) or said composition (B) plus 30° C. or lower; and subsequently
removing the solvent.
2. The method of producing a microporous polyolefin membrane according to claim 1 , wherein said polyolefin (A) has a weight-average molecular weight of 1×10 6 to 15×10 6 .
3. The method of producing a microporous polyolefin membrane according to claim 1 , wherein said polyolefin composition (B) is composed of an ultra-high-molecular-weight polyolefin having a weight-average molecular weight of 1×10 6 to 15×10 6 and a polyolefin having a weight-average molecular weight of 1×10 5 or more but less than 1×10 6 .
4. The method of producing a microporous polyolefin membrane according to claim 1 , wherein said polyolefin composition (B) contains an ultra-high-molecular-weight polyolefin having a weight-average molecular weight of 7×10 5 or more at 1 weight % or more.
5. The method of producing a microporous polyolefin membrane according to any one of claims 1 to 3 , wherein said polyolefin (A) or polyolefin composition (B) has a weight-average molecular weight/number-average molecular weight ratio (Mw/Mn) of 300 or less.
6. The method of producing a microporous polyolefin membrane according to any one of claims 1 to 3 , wherein said polyolefin (A) or polyolefin composition (B) has a weight-average molecular weight/number-average molecular weight ratio (Mw/Mn) of 5 to 50.
7. The method of producing a microporous polyolefin membrane according to any one of claims 1 to 4 , wherein said polyolefin (A) or polyolefin for said composition (B) is polypropylene or polyethylene.
8. The method of producing a microporous polyolefin membrane according to any one of claims 1 to 4 , wherein the following relationships hold for r(MD)=cos 2 ND(b)/cos 2 MD(b) and r(TD)=cos 2 ND(b)/cos 2 TD(b), defined by X-ray analysis of the microporous polyolefin membrane:
100 ≧r ( TD )≧1.3
100 ≧r ( MD )≧3.5
1.0>cos 2 ND ( b )≧0.45.
9. The method of producing a microporous polyolefin membrane according to any one of claims 1 to 4 , wherein said polyolefin composition (B) is composed of a polyolefin having a weight-average molecular weight of 5×10 5 or more and polyolefin having a weight-average molecular weight of 1,000 to 4,000 and melting point of 80 to 130° C.
10. The method of producing a microporous polyolefin membrane according to claim 1 , 3 or 4 , wherein said polyolefin composition (B) is composed of (B- 1 ) an ultra-high-molecular-weight polyolefin having a weight-average molecular weight of 5×10 5 or more and (B- 2 ) a polyolefin having a weight-average molecular weight of 5×10 5 or less, the (B- 2 )/(B- 1 ) weight ratio being 0.2 to 20.
11. The method of producing a microporous polyolefin membrane according to claim 1 , 3 or 4 , wherein said polyolefin composition (B) is composed of a polyolefin having a weight-average molecular weight of 5×10 5 or more and polypropylene having a weight-average molecular weight of 3×10 5 or more.
12. The method of producing a microporous polyolefin membrane according to claim 1 , 3 or 4 , wherein said polyolefin composition (B) is composed of a polyolefin having a weight-average molecular weight of 5×10 5 or more and ethylene-based copolymer having a melting point of 95 to 125° C. and produced in the presence of a single-site catalyst.
13. The method of producing a microporous polyolefin membrane according to claim 1 , 3 or 4 , wherein said polyolefin composition (B) is composed of 1 to 69 weight % of an ultra-high-molecular-weight polyolefin having a weight-average molecular weight of 7×10 5 or more, 98 to 1 weight % of a high-density polyethylene, and 1 to 30 weight % of a low-density polyethylene.
14. The method of producing a microporous polyolefin membrane according to any one of claims 1 to 4 , wherein stretching said gel-like article is an essential step.
15. The method of producing a microporous polyolefin membrane according to claim 14 , wherein said gel-like article is stretched, and thermally set at the stretching temperature or higher but at melting point of said polyolefin (A) or polyolefin composition (B) plus 30° C. or lower.
16. The method of producing a microporous polyolefin membrane according to claim 14 , wherein said stretching step is effected at an areal ratio of 15 to 400.