Dimensionally stable polyester yarn for high tenacity treated cords
View Patent ↗A spun polyester fiber, a drawn polyester yarn, and methods for making them. Polyethylene terephthalate yarn is prepared by extruding a molten melt-spinnable polyethylene terephthalate having an intrinsic viscosity of at least about 0.8 through a shaped extrusion orifice having a plurality of openings to form a molten spun yarn; solidifying gradually said molten spun yarn by passing said molten spun yarn through a solidification zone which comprises (i) a retarded cooling zone and (ii) a cooling zone adjacent said retarded cooling zone where, in said cooling zone, said yarn is rapidly cooled and solidified in a gaseous atmosphere; withdrawing at sufficient speed said solidified yarn from said solidification zone to form a crystalline partially oriented yarn; and hot drawing said crystalline partially oriented yarn at a total draw ratio between about 1.5/1 and about 2.5/1 to produce a drawn yarn having an effective crosslink density (N) between about 10×10 21 and about 20×10 21 crosslinks per cubic centimeter. The yarns and fibers so prepared may be used to make treated tire cord having high tenacity in combination with improved dimensional stability.
1. A process for the production of a drawn polyethylene terephthalate yarn which translates to a high tenacity dimensionally stable tire cord, the process comprising:
(a) extruding a molten melt-spinnable polyethylene terephthalate having an intrinsic viscosity of at least about 0.8 through a shaped extrusion orifice having a plurality of openings to form a molten spun yarn;
(b) solidifying gradually said molten spun yarn by passing said molten spun yarn through a solidification zone which comprises (i) a retarded cooling zone and (ii) a cooling zone adjacent said retarded cooling zone, wherein said cooling zone, said yarn is rapidly cooled and solidified in a gaseous atmosphere;
(c) withdrawing at sufficient speed said solidified yam from said solidification zone to form a crystalline partially oriented yarn; and
(d) hot drawing said crystalline partially oriented yarn at a total draw ratio between 1.5/1 and about 2.5/1 to produce a drawn yarn having an effective crosslink density (N) between about 10×10 21 and about 20×10 21 crosslinks per cubic centimeter; thereby obtaining a drawn yarn with a terminal modulus of at least 20 g/d.
2. The process of claim 1 wherein in said step (d), a draw point localizing jet is used.
3. The process of claim 1 wherein in said step (b), said retarded cooling zone comprises a gaseous atmosphere heated at a temperature of 150°C. to 450°C.
4. The process of claim 1 wherein in said step (b), said retarded cooling zone comprises a heated sleeve.
5. The process of claim 4 wherein said heated sleeve is at a temperature of 220°C. to 300°C.