Filter media and structure
In the filtration of fluid materials, the removal of particulate from the moving stream requires substantial pressure to maintain flow and substantial capacity for removing particulate. The filters of the invention are rugged, high wet strength materials having a basis weight, permeability and efficiency suitable to obtain substantial reduction in particulate loading from liquid streams without plugging or mechanical failure. In particular, the filters of the invention permit the removal of substantial proportions of particulate from non-aqueous streams including lubricant oils, hydraulic fluids and other contaminated streams.
1. A filter medium comprising:
two layers, the layers consisting essentially of,
a loading layer adjacent to an efficiency layer, the efficiency layer having a mean flow pore size smaller than the loading layer, the loading layer consisting essentially of a blend of:
about 5% to 50 wt % of a bicomponent binder fiber,
about 50 to 95 wt % of a media fiber consisting of a glass fiber, and
about 0.5 to 25 wt % of a binder resin,
wherein the loading layer has a basis weight of about 30 to 250 g-m −2 and
wherein the loading layer provides a permeability of 10 to 40 ft-min −1 , and a wet bursting strength of 5 to 50 lb-in −2 , inclusive; and
the efficiency layer consisting essentially of a blend of,
about 5% to 50 wt % of a bicomponent binder fiber,
about 50 to 95 wt % of a media fiber consisting of a glass fiber, and
about 0.5 to 25 wt % of a binder resin,
wherein the efficiency layer has a basis weight of about 30 to 250 g-m −2 and
wherein the efficiency layer provides a permeability of 10 to 40 ft-min −1 , and a wet bursting strength of 5 to 50 lb-in −2 , inclusive.
2. The medium of claim 1 wherein the loading layer has a basis weight of about 30 to 75 g-m −2 .
3. The medium of claim 1 wherein the efficiency layer has a basis weight of about 50 to 150 g-m −2 .
4. The medium of claim 1 wherein the loading layer comprises about 5 to 25 wt % of a bicomponent binder fiber, about 70 to 90 wt % of a glass fiber.
5. The medium of claim 1 wherein the efficiency layer comprises about 5 to 25 wt % of a bicomponent binder fiber, about 50 to 95 wt % of a glass fiber.
6. The medium of claim 1 wherein the glass fiber comprises a blend of two of more glass fiber sources that differ by average diameter each source present in an amount of at least 2%.
7. The medium of claim 1 wherein the medium comprises about 50 to 80 wt % of a glass fiber.
8. The medium of claim 1 wherein the medium comprises about 1 to 20 wt % of a binder resin.
9. The medium of claim 1 wherein either the loading layer or the efficiency layer comprises about 0.5 to 55% of a secondary fiber.
10. The medium of claim 9 wherein the secondary fiber is a polyester fiber.
11. The medium of claim 1 wherein the efficiency layer comprises a wet bursting strength of 5 to 30 lb-in −2 , inclusive and the mean flow pore size ranges from about 2 to about 10 micrometers.
12. The medium of claim 1 wherein the efficiency layer comprises a mean flow pore size of about 4 to about 8 micrometers.
13. A filter cartridge adapted for filtering particulate from a fluid, the filter comprising the media of claim 1 .
14. The filter of claim 13 wherein the filter media comprises at least two layers, the at least two layers comprising,
a loading layer having a basis weight of about 25 to 75 g-m −2 adjacent to an efficiency layer having a basis weight of about 50 to 150 g-m −2 , the loading layer comprises about 1 to 25 wt % of the bicomponent binder fiber, and about 70 to 90 wt % of the glass fiber, the efficiency layer comprises about 5 to 25 wt % of the bicomponent binder fiber, and about 50 to 95 wt % of the glass fiber,
wherein the efficiency layer has a mean flow pore size smaller than the loading layer, the filter provides a permeability of 10 to 40 ft-min −1 , and a wet bursting strength of 10 to 30 lb-in −2 , inclusive.
15. The medium of claim 13 wherein the glass fiber comprises a blend of two or more glass fiber sources that differ by average diameter.
16. The medium of claim 13 wherein the glass fiber comprises a blend of three or more glass fiber sources that differ by average diameter.
17. The medium of claim 13 wherein the medium comprises at least 5 wt % of a bicomponent binder fiber.
18. The medium of claim 13 wherein at least one layer in the medium comprises about 50 to 95 wt % of a glass fiber.
19. The medium of claim 13 wherein the medium comprises about 0 to 25 wt % of a binder resin.
20. The medium of claim 13 wherein the medium comprises a basis weight of about 30 to 228 g-m −2 .
21. The medium of claim 13 wherein the medium comprising a wet bursting strength of 5 to 30 lb-in −2 , inclusive.
22. The medium of claim 13 wherein the medium comprises a mean flow pore size of about 2 to about 10 micrometers.
23. The medium of claim 13 wherein the glass fiber comprises a blend of a first fiber having an diameter of less than 0.5 microns and a second glass fiber having a diameter of greater than 5 microns.
24. A filter loading medium consisting essentially of a medium and an optional support, the medium being a blend of:
about 1 to 15 wt % of a bicomponent binder fiber;
about 50 to 90 wt % consisting of a glass fiber; and
about 0.5 to 25 wt % of a latex resin,
the bicomponent binder fiber, the glass fiber, and the latex resin have a basis weight of about 25 to 75 g-m −2 , and
wherein the bicomponent binder fiber, the glass fiber, and the latex resin provide a permeability of 90 to 160 ft-min −1 , and a wet bursting strength of 5 to 50 lb-in −2 , inclusive.
25. The medium of claim 24 wherein the glass fiber comprises a blend of two or more glass fiber sources that differ by average diameter.
26. The medium of claim 24 wherein the glass fiber comprises a blend of three or more glass fiber sources that differ by average diameter.
27. The medium of claim 24 wherein the medium comprises about 5 wt % to 15 wt % of a bicomponent binder fiber.
28. The medium of claim 24 wherein the medium comprises about 70 to 90 wt % of a glass fiber.
29. The medium of claim 24 wherein the medium comprises about 5 to 10 wt % of a binder resin.
30. The medium of claim 24 wherein the medium comprises a basis weight of about 30 to 60 g-m −2 .
31. The medium of claim 24 wherein the medium comprising a wet bursting strength of 5 to 30 lb-in −2 , inclusive and the mean flow pore size ranges from about 2 to about 10 micrometers.
32. The medium of claim 24 wherein the medium comprises a mean flow pore size of about 2 to about 10 micrometers.
33. The medium of claim 24 wherein the glass fiber comprises a blend of a first fiber having an diameter of less than 0.5 microns and a second glass fiber having a diameter of greater than 5 microns.