Liquid foam systems and ASTM E-84 class 1 rated rigid, high-density polyurethane foams and articles prepared therefrom
An all-liquid foam-forming system contains: a first part (A) containing at least one liquid isocyanate or polyisocyanate; and a second part (B) containing: at least one liquid aromatic polyester polyol having an hydroxyl value of at least 110 mg KOH/gram and an average hydroxyl functionality of at least 2, at least two liquid halogenated flame retardants and water; the foam-forming system having an NCO/OH ratio of from about 0.9:1 to about 1.3:1; wherein the first and second parts are such that reaction therebetween forms a rigid polyurethane foam having a density of at least about 5 pcf and an ASTM E-84 Class 1 rating. Resultant polyurethane foams can be used to make articles, particularly for use in commercial decorative molding applications.
1. An all-liquid foam-forming system for forming a rigid, high density polyurethane foam having a density of at least about 5 pcf and an ASTM E-84 Class 1 rating, consisting of:
a first liquid part (A) consisting of polymethylene polyphenylene polyisocyanates; and
a second liquid part (B) consisting of at least one liquid aromatic polyester polyol having an hydroxyl value of 295-350 mg KOH/gram and a hydroxyl functionality of 2.0-2.2, said at least one liquid aromatic polyester polyol being present in an amount of at least 26% by weight of the combined weight of parts (A) and (B), diethylene glycol, a halogen-substituted organic phosphate and a brominated organic compound, water, at least one liquid tertiary amine for catalyzing reaction between said first liquid part (A) and said aromatic polyester polyol, a triethanolamine propoxylated polyol, from 0 to no more than 2.0% by weight of one or more polyether polyols based on the combined weight of part (A) and part (B), and, optionally, a liquid surfactant;
wherein the system has an NCO/OH ratio of 0.95:1 to 1.2:1 and parts (A) and (B) are provided at a mix ratio (B/A) of 1:0.9 by weight and react to form the rigid, high density polyurethane foam having the ASTM E-84 Class 1 rating and a density of at least about 5 pcf.
2. A system according to claim 1 , wherein the halogen-substituted organic phosphate is tris(2-chloroisopropyl)phosphate and the brominated organic compound is tetrabromophthalate diol.
3. A system according to claim 1 , wherein the halogen-substituted organic phosphate and the brominated organic compound are about 3% to about 16% by weight of the combined weight of the first part (A) and the second part (B).
4. A system according to claim 1 , wherein the halogen-substituted organic phosphate and the brominated organic compound are about 6% to about 14% by weight of the combined weight of the first part (A) and the second part (B).
5. A system according to claim 1 , wherein the halogen-substituted organic phosphate and the brominated organic compound are about 8% to about 12% by weight of the combined weight of parts (A) and (B).
6. A rigid, high-density polyurethane foam having an ASTM E-84 class 1 rating and a density of at least about 5 pcf, consisting of the reaction product between:
a first liquid part (A) consisting of polymeric diphenylmethane diisocyanate, 4,4′-diphenylmethane diisocyanate, and diphenylmethane diisocyanate mixed isomers; and
a second liquid part (B) comprising of at least one aromatic polyester polyol having an hydroxyl value of 295-350 mg KOH/gram and a hydroxyl functionality of 2.0-2.2, diethylene glycol, a halogen-substituted organic phosphate, a brominated organic compound, water, a triethanolamine propoxylated polyol, at least one tertiary amine which catalyzes the reaction between the first liquid part (A) and said at least one aromatic polyester polyol, from 0 to no more than 2.0% by weight of one or more polyether polyols based on the combined weight of part (A) and part (B), and, optionally, a liquid surfactant;
wherein the foam-forming system having an NCO/OH ratio of 0.95:1 to 1.2:1 and parts (A) and (B) are provided at a mix ratio (B/A) of 1:0.9 by weight.
7. A shaped object consisting of the rigid, high-density polyurethane foam according to claim 6 .
8. An all-liquid foam-forming system for forming a rigid, high density polyurethane foam having a density of at least about 5 pcf and an ASTM E-84 Class 1 rating, consisting of:
a first liquid part (A) consisting of 60-100 wt % polymeric diphenylmethane diisocyanate, 20-30 wt % 4,4′-diphenylmethane diisocyanate, and 1-5 wt % 2,4′-diphenylmethane diisocyanate mixed isomers, and
a second liquid part (B) consisting of at least one aromatic polyester polyol having an hydroxyl value of 295-350 mg KOH/g and an hydroxyl functionality of 2.0-2.2, diethylene glycol, a tetrabromophthalate diol having a molecular weight of about 520 and a hydroxyl value of about 215, a tris(2-chloroisopropyl)phosphate flame retardant, water, at least one liquid tertiary amine, a triethanolamine propoxylated polyol, and a liquid silicone surfactant; and
said at least one liquid aromatic polyester polyol being present in an amount of at least 26% by weight of the combined weight of parts (A) and (B);
wherein the system has an NCO/OH ratio of 0.95:1 to 1.2:1; and parts (A) and (B) are provided at a mix ratio (B/A) of about 1:0.9 by weight and react to form the foam having an ASTM E-84 Class 1 rating at a density of at least about 5 pcf.
9. A system according to claim 1 wherein the polymethylene polyphenylene polyisocyanates of the first liquid part (A) consist of polymeric diphenylmethane diisocyanate, 4,4′-diphenylmethane diisocyanate, and diphenylmethane diisocyanate mixed isomers.