Monovinylarene conjugated diene copolymer compositions for acrylate blends
View Patent ↗The present invention relates to monovinylarene-conjugated diene copolymer compositions adapted for blendability with acrylate polymers. In some embodiments, such compositions are provided that are particularly resistant to blocking when stored in pellet form.
1. A composition comprising:
a monovinylarene-conjugated diene block copolymer;
wherein the block copolymer has two modes and three tapered blocks;
wherein the monovinylarene in the three tapered blocks comprises less than 25 wt % of the block copolymer;
wherein the block copolymer comprises at least a first and a second charge of monovinylarene,
wherein the first charge has a weight ratio to the second charge in the range of 1:2 to 2:1;
wherein the block copolymer comprises from 30 to 40 wt % diene;
wherein a monoblock formed from a first charge of monovinylarene in the block copolymer preceding the three tapered blocks has a molecular weight in the range of 25,000 to 65,000 gram per mole; and
wherein the block copolymer has a blocking force of less than 175 lb.
2. The composition of claim 1 , wherein the three tapered blocks comprise less than 18 wt % of the block copolymer.
3. The composition of claim 1 , wherein the block copolymer comprises at least 34 wt % diene.
4. The composition of claim 1 , wherein a monoblock formed from a first charge of monovinylarene in the block copolymer preceding the three tapered blocks has a molecular weight less than 30,000 gram per mole.
5. The composition of claim 1 , wherein the block copolymer has a blocking force of less than 100 lb.
6. The composition of claim 1 , wherein the block copolymer has a blocking force of less than 50 lb.
7. The composition of claim 1 , wherein the block copolymer has a blocking force of less than 10 lb.
8. The composition of claim 1 , wherein each mode of the block copolymer comprises terminal monovinylarene linkages, wherein the terminal monovinylarene linkages collectively comprise less than 10 wt % of the block copolymer.
9. The composition of claim 1 , wherein the block copolymer has a melt flow from 3 to 12 grams per 10 minutes.
10. The composition of claim 1 , wherein the block copolymer has a melt flow from 3.2 to 6.9 grams per 10 minutes.
11. The composition of claim 1 , wherein the monovinylarene contains from 8 to 18 carbon atoms and the conjugated diene contains from 4 to 12 carbon atoms.
12. The composition of claim 1 , wherein the monovinylarene is styrene and the diene is butadiene.
13. The composition of claim 1 , wherein the block copolymer is prepared by coupling the following polymer chains:
S1-S2-B1/S3-B2/S4-B3/S5-Li
S2-B1/S3-B2/S4-B3/S5-Li
wherein S represents monovinylarene blocks, B/S represents tapered blocks of conjugated diene/monovinylarene and Li is residue from a monoalkali metal initiator.
14. The composition of claim 1 , wherein the block copolymer is prepared by the addition of a first initiator charge comprising n-butyl lithium and a second initiator charge comprising n-butyl lithium, and wherein the first initiator charge contains less initiator than the second initiator charge.
15. The composition of claim 1 , wherein the block copolymer is prepared by the addition of at least two charges of an initiator selected from the group comprising n-butyl lithium, sec-butyl lithium, t-butyl lithium, and mixtures thereof.
16. The composition of claim 1 , wherein the three tapered blocks are prepared by the addition of a randomizer selected from the group consisting of tetrahydrofuran, diethyl ether, potassium-tert-amylate, and mixtures thereof.
17. The composition of claim 1 :
wherein the monovinylarene is styrene and the diene is butadiene;
wherein the monovinylarene in the three tapered blocks comprises less than 20 wt % of the block copolymer;
wherein the block copolymer comprises at least 34 wt % diene; and
wherein the block copolymer has a blocking force of less than 50 lb.
18. The composition of claim 17 , wherein a monoblock formed from a first charge of monovinylarene in the block copolymer preceding the three tapered blocks has a molecular weight less than 30,000 gram per mole.
19. The composition of claim 17 , wherein the monovinylarene in the three tapered blocks comprises less than 18 wt % of the block copolymer.
20. The composition of claim 17 , wherein the monovinylarene in the three tapered blocks comprises less than 16 wt % of the block copolymer.
21. A method of producing a monovinylarene-conjugated diene block copolymer suited for blending with monovinylarene acrylate copolymers, comprising:
sequentially contacting under polymerization conditions at least one monovinylarene monomer, an organomonoalkali metal initiator, at least one conjugated diene monomer, and thereafter coupling with a polyfunctional coupling agent to form the block copolymer;
wherein the block copolymer has two modes and three tapered blocks;
wherein the monovinylarene is styrene and the diene is butadiene;
wherein the monovinylarene in the three tapered blocks comprises less than 18 wt % of the block copolymer;
wherein the block copolymer comprises at least a first and a second charge of monovinylarene, wherein the first charge has a weight ratio to the second charge in the range of 1:2 to 2:1;
wherein the block copolymer comprises from 34 to 40 wt % diene;
wherein a monoblock formed from a first charge of monovinylarene in the block copolymer preceding the three tapered blocks has a molecular weight in the range of 25,000 to 65,000 gram per mole; and
wherein the block copolymer has a blocking force of less than 50 lb.
22. A composition comprising:
a monovinylarene-conjugated diene block copolymer;
wherein the block copolymer has two modes and three tapered blocks;
wherein the monovinylarene is styrene and the diene is butadiene;
wherein the monovinylarene in the three tapered blocks comprises less than 20 wt % of the block copolymer;
wherein the block copolymer comprises at least 34 wt % diene; and
wherein the block copolymer has a blocking force of less than 50 lb.
23. The composition of claim 22 , wherein the block copolymer comprises at least a first and a second charge of monovinylarene, and wherein the first charge has a weight ratio to the second charge in the range of 1:3 to 3:1.
24. The composition of claim 22 , wherein the block copolymer comprises at least a first and a second charge of monovinylarene, and wherein the first charge has a weight ratio to the second charge in the range of 1:2 to 2:1.
25. A composition comprising:
a monovinylarene-conjugated diene block copolymer;
wherein the block copolymer has at least two modes;
wherein the monovinylarene in a tapered portion comprises less than 25 wt % of the block copolymer;
wherein the block copolymer comprises at least a first and a second charge of monovinylarene,
wherein the first charge has a weight ratio to the second charge in the range of 1:2 to 2:1;
wherein the block copolymer comprises from 30 to 40 wt % diene;
wherein a monoblock formed from a first charge of monovinylarene in the block copolymer preceding the tapered portion has a molecular weight in the range of 25,000 to 65,000 gram per mole;
wherein the block copolymer has a blocking force of less than 175 lb; and
wherein the block copolymer is prepared by coupling the following polymer chains:
S1-S2-B1/S3-B2/S4-B3/S5-Li
S2-B1/S3-B2/S4-B3/S5-Li
wherein S represents monovinylarene blocks, B/S represents tapered blocks of conjugated diene/monovinylarene, and Li is residue from a monoalkali metal initiator.