Carbon black with large primary particle size as reheat additive for polyester and polypropylene resins
View Patent ↗Reheat characteristics of polyethylene and polypropylene resins, including reheating time and resin color, are improved by adding to the resin carbon black with a primary particle size in the range of 200 to 500 nm as an infrared absorber. Thermal carbon blacks having this primary particle size are preferred over Furnace carbon blacks. Injection stretch-blow molded bottles and other thermoformed products are made from resins with carbon black infrared absorber.
1. A method for forming polyethylene terephthalate resins with improved reheat performance, comprising:
adding to the resin from 2 ppm to 50 ppm by weight of carbon black, based on the weight of the resin composition including the carbon black, wherein the carbon black has a primary particle with a diameter in the range of 200 nm to 500 nm, further wherein a 4 mm thick by 10 cm diameter plaque injection molded from the resin has an L* value of greater than about 67, measured by reflection when placed on a white tile.
2. The method of claim 1 , wherein the carbon black is present in a concentration of from 3 ppm to 50 ppm by weight.
3. The method of claim 1 , wherein the carbon black is present in a concentration of from 5 ppm to 50 ppm by weight.
4. The method of claim 1 , wherein the carbon black is present in a concentration of from 5 ppm to 15 ppm by weight.
5. The method of claim 1 , wherein the carbon black has a primary particle with a diameter in the range of 250 nm to 500 nm.
6. The method of claim 1 , wherein the carbon black has a primary particle with a diameter in the range of 250 nm to 300 nm.