Ultraviolet radiation cured powder coatings for stained wood
View Patent ↗The present invention provides smooth and even ultraviolet (UV) cured powder coatings for wood comprising one, two or three layers of one or more waterborne stains, or clear or tinted waterborne basecoat coatings and one or more topcoat layers of clear or tinted clear powder coatings made from one or more than one free radical UV curing resin, one or more than one photoinitiator, and one or more than one post-blend dry flow additive, such as fumed alumina. The coatings of the present invention have a natural wood appearance, are foam free and fully coat substrates at powder coating thicknesses ranging from 0.5 mil (12.7 μm) to 2.0 mil (50.8 μm). Accordingly, the coatings will fully and evenly coat uneven, beveled and/or routered substrate surfaces, including open grain natural wood substrates, such as oak. In addition, the present invention provides a method for making coatings comprising applying one or more waterborne stain to the wood to form a stain layer, drying or curing the said stain layer, sanding or grinding to de-nibb the said stain layer, applying clear or tinted UV curing coating powder to the stained substrate, flowing out the applied coating powder to form a continuous film, and UV curing the film formed from the powder.
1. A smooth and even coating on a wood substrate comprising:
one, two or three layers of one or more waterborne stain or tinted waterborne basecoat; and,
one or more topcoat layers of clear or tinted clear powder coatings comprising one or more than one free radical UV curing resin, one or more than one photoinitiator, and one or more than one post-blend dry flow additives,
wherein the said powder coating is formed from a coating powder having an average particle size of from 5 to 25 μm.
2. A coating as claimed in claim 1 , wherein the total thickness of the said one or more topcoat layers ranges from 0.5 mil (12.7 μm) to 2.0 mil (50.8 μm).
3. A coating as claimed in claim 1 , wherein the said powder coating further comprises one or more than one crystalline crosslinker resin.
4. A coating as claimed in claim 3 , wherein the said one or more than one crystalline crosslinker resin comprises vinyl ether resin.
5. A coating as claimed in claim 1 , wherein the said substrate has an uneven, curvilinear, beveled or routered surface, or a combination thereof.
6. A coating as claimed in claim 1 , wherein the said substrate is chosen from open grain natural wood and close grain natural wood.
7. A method for making a coating as claimed in claim 1 comprising:
providing one or more waterborne stain compositions and one or more clear or tinted UV curing coating powder,
applying the said one or more waterborne stain to the wood to form a stain layer,
drying or curing the said stain layer,
sanding or grinding to de-nibb the said stain layer,
applying the said clear or tinted UV curing coating powder to the stained substrate,
flowing out the applied coating powder to form a continuous film, and UV curing the film formed from the powder.
8. A method for making a coating as claimed in claim 7 , further comprising pre-sanding or pre-grinding the said surface prior to applying said waterborne stain.
9. A method for making a coating as claimed in claim 7 , further comprising pre-heating the said stained substrate surface prior to applying said UV curing coating powder.