High-cleaning/low abrasive silica and materials and dentifrice containing such materials
View Patent ↗Unique abrasive and/or thickening materials that are in situ generated compositions of precipitated silicas and silica gels are provided. Such compositions exhibit different beneficial characteristics depending on the structure of the composite in situ generated material. With low structured composites (as measured via linseed oil absorption levels from 40 to 100 ml oil absorbed/100 g composite), simultaneously high pellicle film cleaning properties and moderate dentin abrasion levels are possible in order to accord the user a dentifrice that effectively cleans tooth surfaces without detrimentally abrading such surfaces. Increased amounts of high structure composite materials tend to accord greater viscosity build and thickening benefits together with such desirable abrasion and cleaning properties, albeit to a lesser extent than for the low structure types. Thus, mid-range cleaning materials will exhibit oil absorption levels from an excess of 100 to 150, and high thickening/low abrasion composite exhibit oil absorption properties in excess of 150. Such an in situ, simultaneously produced precipitated silica/silica gel combination provides such unexpectedly effective low abrasion and high cleaning capability and different thickening characteristics as compared to physical mixtures of such components. Encompassed within this invention is a unique method for making such gel/precipitated silica composite materials for such a purpose, as well as the different materials within the structure ranges described above and dentifrices comprising such.
1. An in situ produced gel/precipitate silica combination, wherein said composite comprises from 10 to 60% by volume of silica gel, wherein said composite exhibits a linseed oil absorption of greater than 100 up to 150 ml/100 g, and wherein said composite exhibits a 10% Brass Einlehner hardness value in the range between about 2.5 and 12 mg loss/100,000 revolutions.
2. The combination of claim 1 wherein said combination comprises from 20 to 33% by volume of silica gel.
3. The in situ produced gel/precipitate silica composite of claim 1 wherein said composite is in the form of particles exhibiting a median particle size range of from 3 to 20 microns.
4. The in situ produced gel/precipitate silica composite of claim 2 wherein said composite is in the form of particles exhibiting a median particle size range of from 3 to 20 microns.
5. A dentifrice formulation comprising the composite as defined in claim 1 .
6. A dentifrice formulation comprising the composite as defined in claim 2 .
7. A dentifrice formulation comprising the composite as defined in claim 3 .
8. The dentifrice formulation of claim 5 further comprising an abrasive material other than said composite.
9. The dentifrice formulation of claim 6 further comprising an abrasive material other than said composite.
10. The dentifrice formulation of claim 7 further comprising an abrasive material other than said composite.
11. A method of producing the composite as defined in claim 1 , said method comprising the sequential steps of
a) admixing a sufficient amount of an alkali silicate having a concentration of from 4 to 35% by weight within an aqueous solution thereof and an acidulating agent having an acid concentration within an aqueous solution thereof of from 5 to 25% by weight together at a temperature from about 40 to about 90° C. and under agitation to form a composition comprising silica gel particles; and, without first washing, modifying, or purifying said formed composition,
b) subsequently introducing to said composition a sufficient amount of an alkali silicate and an acidulating agent to form a precipitated silica, thereby producing a gel/precipitate silica composite, wherein the pH of the overall reaction is within the range of from 3 to 10.
12. The method of claim 11 wherein the acid concentration in step “a” is from 10 to 20%.
13. An in situ produced gel/precipitate silica composite, wherein said combination comprises from 10 to 60% by volume of silica gel, wherein when said composite is introduced as the sole abrasive component within a dentifrice composition said dentifrice composition exhibits a PCR:RDA (Pellic Cleaning Ratio Radioactive Dentin Abrasion) ratio of from about 0.7 to about 1.1, a PCR value between about 90 and 110, and a RDA level of between about 95 and about 150.
14. The combination of claim 13 wherein said composite comprises from 20 to 33% by volume of silica gel.
15. A dentifrice formulation comprising the composite as defined in claim 13 .
16. A dentifrice formulation comprising the composite as defined in claim 14 .
17. The dentifrice formulation of claim 15 further comprising an abrasive material other than said composite.
18. The dentifrice formulation of claim 16 further comprising an abrasive material other than said composite.
19. A method of producing the composite as defined in claim 13 , said method comprising the sequential steps of
a) admixing a sufficient amount of an alkali silicate having a concentration of from 4 to 35% by weight within an aqueous solution thereof and an acidulating agent having an acid concentration within an aqueous solution thereof of from 5 to 25% by weight together at a temperature from about 40 to about 90° C. and under agitation to form a composition comprising silica gel particles; and, without first washing, modifying, or purifying said formed composition,
b) subsequently introducing to said silica gel composition a sufficient amount of an alkali silicate and an acidulating agent to form a precipitated silica, thereby producing a gel/precipitate silica composite, wherein the pH of the overall reaction is within the range of from 3 to 10.
20. The method of claim 19 wherein the acid concentration in step “a” is from 10 to 20%.