Ultrafast and ultrasensitive hydrogen sensors based on self-assembly monolayer promoted 2-dimensional palladium nanoclusters
View Patent ↗A device and method of making same. The device or hydrogen detector has a non-conducting substrate with a metal film capable of absorbing hydrogen to form a stable metal hydride. The metal film is being on the threshold of percolation and is connected to mechanism for sensing a change in electrical resistance in response to the presence of hydrogen in contact with the metal film which causes an increase in conductivity.
1. A device, comprising a non-conducting substrate having thereon, a metal film comprised of nanoclusters of metal atoms capable of absorbing hydrogen to form a stable metal hydride, said metal film being on the threshold of percolation, and mechanism in electrical communication with said metal film for sensing a change in electrical resistance in response to the presence of hydrogen in contact with said metal film, whereby hydrogen absorbed by said metal film forms a metal hydride larger in volume than the metal resulting in percolation of said metal film and an increase in the conductivity thereof; and wherein said non-conducting substrate has a stiction-reducing coating thereon.
2. The device of claim 1 , wherein said metal nanoclusters have an average diameter of less than about 10 nanometers.
3. The device of claim 1 , wherein many of said metal nanoclusters are mobile with respect to each other.
4. The device of claim 3 , wherein non-conducting substrate has a self-assembled layer thereon.
5. The device of claim 4 , wherein said non-conducting substrate has a siloxane coating thereon which is substantially a monolayer.
6. The device of claim 5 , wherein the siloxane is an alkylsilane.
7. The device of claim 6 , wherein the alkylsilane contains chlorine atoms.
8. The device of claim 7 , wherein the silane is octadecyl trichlorosilane.
9. The device of claim 5 , wherein the alkylsilane contains fluorine atoms.
10. The device of claim 9 , wherein the alkylsilane is fluorinated undecyl trichlorosilane.
11. The device of claim 4 , wherein the self-assembled layer is a carboxy terminated alkylsilane.
12. The device of claim 1 wherein said non-conducting substrate has a hydrophobic surface.
13. The device of claim 1 wherein said metal film on the threshold of percolation has a thickness of less than about 10 nm.
14. The device of claim 1 wherein said metal film on the threshold of percolation is less than about 5 nanometers thick.
15. The device of claim 1 wherein said metal film on the threshold of percolation is between 3.3 and 3.6 nanometers thick.
16. The device of claim 1 , wherein said metal film is one or more of Pd, Cu, Au, Ni, Rh, Pt, Y, La or alloys thereof.
17. The device of claim 1 , wherein said metal film is Pd or an alloy thereof.
18. A method of making a device, comprising providing a non-conducting substrate with a coating thereon having a low surface free energy, depositing a metal film capable of absorbing hydrogen to form a stable metal hydride on or in association with the substrate, the metal film being on the threshold of percolation, and establishing mechanism in electrical communication with the metal film for sensing a change in electrical resistance in response to the presence of hydrogen in contact with the metal film, whereby hydrogen absorbed by the metal film forms a metal hydride larger in volume than the metal resulting in percolation of the metal film and an increase in the conductivity thereof.
19. The method of claim 18 , wherein the substrate surface has low surface free energy.
20. The method of claim 18 , wherein the substrate is hydrophobic.
21. The method of claim 18 , wherein the metal film includes mobile metal nanoclusters.
22. The method of claim 21 , wherein the metal nanoclusters are one or more of Pd, Cu, Au, Ni, Rh, Pt, Y, La or alloys thereof.
23. The method of claim 22 , wherein the metal nanoclusters are Pd or alloys thereof.
24. The method of claim 23 , wherein the substrate has a self assembled siloxane layer thereon.
25. The method of claim 24 , wherein the self assembled layer is substantially a monolayer.
26. The method of claim 25 , wherein the metal film has a thickness less than about 10 nanometers.
27. A device, comprising a non-conducting substrate having thereon a non-metallic material intermediate said substrate and a metal film formed of nanoclusters of metal atoms capable of absorbing hydrogen to form a stable metal hydride, said metal film being on the threshold of percolation, and mechanism in electrical communication with said metal film for sensing a change in electrical resistance in response to the presence of hydrogen in contact with said metal film, whereby hydrogen absorbed by said metal film forms a metal hydride larger in volume than the metal resulting in percolation of said metal film and an increase in the conductivity thereof; and wherein said non-conducting substrate has a stiction-reducing coating thereon.