Process for recovering lead oxides from exhausted batteries
View Patent ↗A process for recovering lead oxides from the spent paste of exhausted lead acid batteries. The process provides heating the spent paste with an alkali hydroxide solution at elevated temperatures prior to calcinations. Calcination is at various temperatures so that either lead mono-oxide, lead dioxide or red lead is obtained as the principal product. There is also provided the use of the lead oxide to prepare the paste for positive and negative electrodes or other lead compounds.
1. A process for separating and producing lead oxides in a substantially pure state from spent paste obtained from exhausted lead acid batteries, which comprises the steps of:
A) treating spent paste obtained from exhausted lead acid batteries with an alkali hydroxide solution,
B) heating the mixture obtained from step “A” at a temperature between 40-100° C.,
C) filtering the mixture from step “B” and washing the filter cake formed with water, and then
D) heating the filter cake from step “C” at a temperature in increments between 350-500° C. and red lead is obtained.
2. The process of claim 1 wherein the filter cake of step “C” is washed with water until a pH of about 9.0 or less is obtained.
3. The process of claim 1 wherein the alkali hydroxide solution in step “A” is selected from the group consisting of sodium hydroxide and potassium hydroxide.
4. The process according to claim 1 wherein the concentration of the alkali hydroxide solution used is between 20-60%.
5. The process of claim 1 wherein the pH of the spent paste of step “A” is brought to a pH of at least 10.
6. The process of claim 5 wherein the pH is 14.
7. The process of claim 1 wherein the spent battery paste of the anode is kept separate and processed separately.
8. The process of claim 1 wherein the spent battery paste of the cathode is kept separate and processed separately.