Non-asphaltic peel and stick roofing product for faster installation
View Patent ↗The present invention provides a non-asphaltic peel-and-stick roofing membrane for quicker and easier installation to a roof substrate, as well as a method of manufacturing the membrane.
1. A self-adhering peel-and-stick roofing membrane comprising:
a. a thermoplastic single-ply membrane having a lower surface and an upper surface, the lower surface having a first pressure sensitive adhesive layer coated thereon and a first removable release liner on the first pressure sensitive adhesive layer, the upper surface having a side lap area defined at one lengthwise border of the membrane and extending longitudinally thereon;
b. optionally a primer and/or cleaner layer applied on the side lap area;
c. a second pressure sensitive adhesive layer coated on the side lap area or on the optional primer and/or cleaner applied on the side lap area;
d. a removable release liner applied on the second pressure sensitive adhesive layer;
e. a reduced area, the reduced area being located on the first pressure sensitive adhesive layer on the lower surface of the membrane, the reduced area corresponding to the second pressure sensitive coated on the side lap area on the upper surface of the membrane, in which the reduced area is reduced or equal to the thickness of the second pressure sensitive adhesive layer coated on the side lap area.
2. The membrane as recited in claim 1 , wherein the first adhesive layer on the lower surface of the membrane in the reduced area corresponding to the side lap area on the upper surface of the membrane is reduced more than the thickness of second adhesive layer on the side lap on the upper surface of the membrane.
3. The membrane as recited in claim 1 , wherein the first adhesive layer on the lower surface of the membrane in the reduced area corresponding to the side lap area on the upper surface of the membrane is reduced less than the thickness of the second adhesive layer on the side lap on the upper surface of the membrane.
4. The membrane as recited in claim 1 , wherein the width of the side lap is in the range of from approximately 1 inch to 20 inches.
5. The membrane as recited in claim 4 , wherein the width of the side lap is in the range of from approximately 3 inches to 6 inches.
6. The membrane as recited in claim 1 , wherein the single-ply membrane is selected from the group consisting of: modified bitumen or thermoset or thermoplastic membrane preferably polyvinyl chloride (PVC) and other resinous compositions containing polyvinyl chloride, chlorosulfonated polyethylene (CSPE or CSM), chlorinated polyethylene (CPE), ethylene propylene diene terpolymer (EPDM), APP modified bitumen, SBS modified bitumen, or a thermoplastic olefin (TPO).
7. The membrane as recited in claim 1 , wherein the primer and/or cleaner is selected from the group consisting of heptanes, toluene, methyl alcohol, hexane, xylene, diphenylmethane diisocyanate, polymethylene polyphenol isocyanate, ethylbenzene, naphtha, hydrocarbon resins or halogenated butyl or a suitable mixture thereof, wherein the mixture has a flash point between 40 and 250° F.
8. The membrane as recited in claim 1 , wherein the adhesive material in first and second pressure sensitive adhesive layers are selected from the group consisting of polyisobutenes (PIB), polybutenes, polyisoprene, butyl rubber, styrene-isoprene-styrene (SIS), styrene-butadiene-styrene (SBS), styrene-ethylene-butadiene-styrene (SEBS), acrylics, polyurethanes, atactic polypropylene (APP) or a suitable mixture thereof.
9. The membrane as recited in claim 1 , wherein the release liner is selected from the group consisting of waxed paper, polycoated paper, film-based paper or plastic.
10. A method of preparing a self-adhering peel-and-stick roofing membrane, the method comprising the steps of:
a. providing a length of a thermoplastic single-ply membrane having a lower surface and an upper surface, the lower surface having a first pressure sensitive adhesive layer coated thereon and a release liner on the first pressure sensitive adhesive layer, the upper surface having a side lap area defined at one lengthwise border of the membrane and extending longitudinally thereon;
b. optionally pre-priming and pre-cleaning the side lap of a single-ply membrane;
c. coating the side lap area or the optionally pre-primed and pre-cleaned side lap area with a second pressure sensitive adhesive layer having a thickness that is 10% to 90% of the thickness of the first adhesive layer;
d. applying a release liner on the second adhesive layer;
e. providing the first pressure sensitive adhesive layer with a reduced area portion, the reduced area portion corresponding to the second pressure sensitive adhesive layer of the side lap area, the reduced area portion being reduced or equal to the thickness of the second pressure sensitive adhesive layer; and
f. rolling the membrane for storage and later application on a roof substrate.
11. The method as recited in claim 10 , wherein the adhesive material in the second pressure sensitive adhesive layer may be the same or a compatible adhesive as the first pressure sensitive adhesive layer.
12. The method as recited in claim 10 , wherein the release liner is selected from the group consisting of waxed paper, polycoated paper, film-based paper or plastic.
13. The method as recited in claim 10 , wherein the width of the side lap is in the range of from approximately 1 inch to 20 inches.
14. The method as recited in claim 13 , wherein the width of the side lap is in the range of from approximately 3 inches to 6 inches.
15. The method as recited in claim 10 , wherein the single-ply membrane is selected from the group consisting of: modified bitumen or thermoset or thermoplastic membrane preferably polyvinyl chloride (PVC) and other resinous compositions containing polyvinyl chloride, chlorosulfonated polyethylene (CSPE or CSM), chlorinated polyethylene (CPE), ethylene propylene diene terpolymer (EPDM), APP modified bitumen, SBS modified bitumen, or a thermoplastic olefin (TPO).
16. The method as recited in claim 10 , wherein the primer and/or cleaner is selected from the group consisting of heptanes, toluene, methyl alcohol, hexane, xylene, diphenylmethane diisocyanate, polymethylene polyphenol isocyanate, ethylbenzene, naphtha, hydrocarbon resins or halogenated butyl or a suitable mixture thereof.
17. The method as recited in claim 10 , wherein the adhesive material in first and second pressure sensitive adhesive layers are selected from the group consisting of polyisobutenes (PIB), polybutenes, polyisoprene, butyl rubber, styrene-isoprene-styrene (SIS), styrene-butadiene-styrene (SBS), styrene-ethylene-butadiene-styrene (SEBS), acrylics, polyurethanes, atactic polypropylene (APP) or a suitable mixture thereof.