Method of preparing storage phosphors from dedicated precursors
View Patent ↗A method for producing CsX:Eu stimulable phosphors and screens or panels provided with said phosphors as powder phosphors or vapor deposited needle-shaped phosphors suitable for use in image forming methods for recording and reproducing images of objects made by high energy radiation, wherein said CsX:Eu stimulable phosphors are essentially free from oxygen in their crystal structure, and wherein X represents a halide selected from the group consisting of Br, Cl and combinations thereof, and wherein the method further comprises the steps of mixing CsX with a compound or combinations of precursor compounds having as a composition Cs x Eu y X′ x+αy , wherein the ratio of x to y exceeds a value of 0.25, wherein α≧2 and wherein X′ is a halide selected from the group consisting of Cl, Br and I and combinations thereof; heating said mixture at a temperature above 450° C.; cooling said mixture, and optionally annealing and recovering said CsX:Eu phosphor.
1. A method for producing a binderless phosphor screen or panel comprising the steps of providing a CsX:Eu phosphor prepared according to a method for producing a CsX:Eu stimulable phosphor, wherein X represents a halide selected from the group consisting of Br, Cl and combinations thereof, comprising the steps of
mixing CsX with a precursor compound or combinations of precursor compounds having as a composition Cs x Eu y X′ x+αy , wherein x/y>0.25, wherein α≧2 and wherein X′ is a halide selected from the group consisting of Cl, Br and I and combinations thereof;
heating said mixture at a temperature above 450° C.
cooling said mixture, and
optionally, recovering said CsX:Eu phosphor and depositing said phosphor on a substrate by a method selected from the group consisting of physical vapor deposition, chemical vapor deposition and an atomization technique.
2. A method for producing a binderless phosphor screen or panel on a substrate containing a CsX:Eu stimulable phosphor, wherein X represents a halide selected from the group consisting of Br, Cl and combinations thereof, said method comprising the steps of:
bringing in a deposition chamber, evacuated to 1 mbar or less and further adding an inert gas thereto, together with said substrate, multiple heatable containers containing CsX and a precursor compound or a combination of precursor compounds having as a composition Cs x Eu y X′ x+αy , wherein X′ is a halide selected from the group of Cl, Br and I and combinations thereof, wherein x/y>0.25s, and wherein α≧2,
further depositing on said substrate, by a method selected from the group consisting of physical vapor deposition, chemical vapor deposition and an atomization technique, said CsX:Eu stimulable phosphor,
wherein said precursor compound or a combination of precursor compounds having as a composition Cs x Eu y X′ x+3y or Cs x Eu y X′ x+2y is present in a ratio to CsX that on said substrate a CsX:Eu storage phosphor is formed, wherein Eu is present as a dopant in an amount between 10 −5 and 5 mol %.
3. A method for producing a phosphor screen or panel on a substrate containing a CsX:Eu stimulable phosphor, wherein X represents a halide selected from the group consisting of Br, Cl and combinations thereof, said method comprising the steps of:
bringing in a deposition chamber, evacuated to 1 mbar or less, together with said substrate, multiple heatable containers containing CsX and a compound or a combination of precursor compounds having as a composition Cs x Eu y X′ x+αy , wherein X′ is a halide selected from the group of Cl, Br and I and combinations thereof, wherein x/y>0.25, and wherein wherein α≧2,
further depositing on said substrate, by a method selected from the group consisting of physical vapor deposition, chemical vapor deposition and an atomization technique, said CsX:Eu stimulable phosphor, wherein said precursor compound or a combination of precursor compounds have as a composition Cs x Eu y X′ x+αy .
4. Method according to claim 3 , wherein in one crucible CsBr is present, while in a second crucible Cs x Eu y Br x+αy , wherein x/y>0.25, and wherein wherein α≧2 is present, optionally in the presence of another amount of CsBr.
5. Method according to claim 3 , wherein in one crucible CsBr and Cs x Eu y Br x+αy , wherein x/y>0.25, and wherein wherein α≧2 is present, while in a second crucible Cs x Eu y Br x+αy is provided.