Dissolving metal particles from supported catalyst using ultrasonic energy, solvent and etchant
A sample preparation method for characterization of nanoparticles embedded in the supports of heterogeneous catalysts, with improved particle dispersion, is introduced. The supported catalyst is first ground or milled into fine powder. Then, the powder is mixed into an organic solvent, and an etchant is added to the solvent to digest the supports and release metallic nanoparticles. The resulting solution is then placed in an ultrasonic bath where ultrasonic waves are generated and applied to the solution. The ultrasonic waves suppress agglomeration of the particles and also break up those particle clusters resulting from agglomeration during the prior steps. Subsequently, a sample is extracted from the solution and prepared for analysis.
1. A method of preparing a characterization sample from a supported catalyst having metal particles dispersed throughout the support material, comprising the steps of:
introducing the supported catalyst having metal particles into a liquid;
adding an etchant into the liquid to separate the metal particles from its support material;
applying ultrasonic energy to the liquid comprising the etchant and the metal particles; and
after the step of applying, extracting a sample volume of the liquid comprising the etchant and the metal particles,
wherein the ultrasonic energy is applied for about 1 hour and then stopped, and the sample volume is extracted 12 to 24 hours after stopping of the ultrasonic energy.
2. The method according to claim 1 , wherein the support material comprises alumina and the etchant comprises HF acid.
3. The method according to claim 2 , wherein the liquid comprising the etchant has an HF concentration of about 20-25% by weight.
4. The method according to claim 1 , wherein the liquid comprises ethanol.
5. The method according to claim 1 , wherein the metal particles comprise nanometer sized platinum particles.
6. The method according to claim 1 , further comprising the step of grinding the supported catalyst into fine powder form prior to introducing it into the liquid.
7. A method of preparing a characterization sample from a supported catalyst having platinum metal particles dispersed throughout the support material, comprising the steps of:
introducing the supported catalyst having platinum metal particles into a liquid;
adding HF acid into the liquid to separate the platinum metal particles from its support material;
applying ultrasonic energy to the liquid comprising the HF acid and the platinum metal particles; and
after the step of applying, extracting a sample volume of the liquid comprising the HF acid and the platinum metal particles wherein the ultrasonic energy is applied for about 1 hour and then stopped, and the sample volume is extracted 12 to 24 hours after stopping of the ultrasonic energy.
8. The method according to claim 7 , wherein the liquid comprising the HF acid has an HF concentration of about 20-25% by weight.
9. The method according to claim 7 , wherein the liquid comprises ethanol.
10. The method according to claim 7 , wherein the support material comprises alumina.