Method and apparatus for making building panels having low edge thickness swelling
An improvement to existing board manufacturing process which utilize lignocellulose particles is described wherein the adhesive to be applied as a binder is at least partly applied before the particles are dried. Using the invention improvement in resin application rates without increase in the water content of the particles fed to a press is achieved. Reduction in edge thickness swelling has been achieved.
1 - 19 . (canceled)
20 . A building panel made from a mixture of lignocellulosic particles and resin binder produced by a process comprising the steps of:
obtaining a source of green lignocellulosic particles,
adding a resin binder to the green particles before the green particles are dried,
drying the green particles to obtain dried particles,
consolidating the dried particles under heat and pressure to obtain a building panel, when the resin is a phenol formaldehyde resin to which is subjected to said drying in the presence of methyol urea.
21 . (canceled)
22 . A process for making building panels from a mixture of lignocellulosic particles and resin binder, said process comprising:
obtaining a source of green lignocellulosic particles,
adding a resin binder to the green particles before the green particles are dried,
drying the green particle to obtain dried particles,
consolidating the dried particles under heat and pressure to obtain a building panel, when the resin is a phenol formaldehyde resin to which is subjected to said drying in the presence of methyol urea,
wherein live steam is injected into the dried particles during the consolidating step.
23 . A process of assuring the production of building panels comprised of a mass of lignocellulosic particles to which an adhesive has been applied, but dried for an extended period before pressing, said process comprising:
admixing said lignocellulosic particles and an adhesive comprising phenol formaldehyde;
drying said particles and adhesive;
applying additive adhesive to the dried particles and adhesive; and
consolidating the particles into a mat by subjecting the particles and adhesive to elevated temperatures and pressure for a time sufficient to cure the adhesive, wherein live steam is injected into the dried particles during the consolidating step.
24 . The process of claim 22 wherein the adhesive that is applied to the lignocellulose particles prior to live steam injection does not contain MDI.
25 . The process of claim 23 wherein the adhesive that is applied to the lignocellulose particles prior to live steam injection does not contain MDI.
26 . A building panel made by the steam injection process of claim 22 .
27 . A building panel made by the steam injection process of claim 23 .
28 . A building panel made by the process of claim 24 .
29 . A building panel made by the process of claim 25.