Eco-friendly photo-fenton catalyst-immobilized Fe(III) over HY-zeolite
View Patent ↗This invention presents preparation, characterization and evaluation of an efficient heterogeneous Fe (III)-HY catalyst for photo-assisted Fenton reaction. Fe (III) ions are immobilized on HY zeolite using different loadings by impregnation, calcination and the activity of the catalyst is evaluated by the degradation of phenol. The effect of Fe loadings, H 2 O 2 concentration, pH and quenching on photo-Fenton reaction are studied. The results obtained clearly show that Fe (III)-HY is efficient in the degradation of phenol and it is compared with that of a homogeneous photo-Fenton reaction. The increased rate of reaction on Fe (III)-HY highlights the synergistic role of zeolite. Heterogeneous Fe (III)-HY in photo-Fenton reaction allows a wide range of pH for reaction against the narrow pH range in homogeneous system. The system is further subjected to evaluate its stability in solid state. The stability of the catalyst is further established by recycling studies.
1. A photo-Fenton catalyst consisting of immobilized Fe(III) on HY-zeolite support, wherein the Fe(III) occupies cationic sites in the support.
2. The catalyst of claim 1 , wherein the Fe(III) loading on the zeolite support is in the range of 0.125 wt % to 5 wt %.
3. The catalyst of claim 1 , wherein the Fe(III) loading on the zeolite support is 0.25 wt %.
4. A method for the preparation of a photo-Fenton catalyst consisting of immobilized Fe(III) on HY-zeolite support, the process comprising loading a Fe(III) precursor onto a HY-zeolite support and then calcining the loaded support to obtain a Fe(III) loaded HY-zeolite catalyst, wherein the Fe(III) on HY-zeolite support occupies cationic sites in the HY-zeolite support.
5. The method of claim 4 , wherein the method comprises wet impregnation wherein a desired weight of inorganic precursor, Fe(III) was dissolved in water and zeolite was added to this solution, soaked for 12 h under continuous stirring, and dried at 100° C., and thereafter calcined at 450° C. for 6 h.
6. The method of claim 5 , wherein the Fe(III) precursor is Fe(NO 3 ) 3 9H 2 O.
7. The method of claim 4 , wherein the Fe(III) loading on the zeolite support is in the range of 0.125 wt % to 5 wt %.
8. The method of claim 4 , wherein the Fe(III) loading on the zeolite support is 0.25 wt %.