Liquid water impermeable reinforced nonwoven fire blocking fabric, method for making such fabric, and articles fire blocked therewith
View Patent ↗This invention relates to a thin reinforced nonwoven fabric comprising a liquid impervious polymeric layer, a compressed web of crimped fiber, a binder, and a reinforcing scrim. The fabric bulks when exposed to heat or flame and is useful as a component for fire blocking mattresses, upholstery, and the like.
1. A reinforced nonwoven fabric for fire blocking an article, comprising a liquid water impermeable polymeric layer and an open mesh scrim having a first side and a second side, the first side of the scrim having crimped, heat-resistant organic fibers compressed thereon and held in a compressed state by a thermoplastic binder,
wherein when the fabric is exposed to heat or flame, the fabric is capable of increasing its thickness by at least two times.
2. The reinforced nonwoven fabric of claim 1 wherein the fabric is capable of tripling its thickness when the fabric is exposed to heat or flame.
3. The reinforced nonwoven fabric of claim 1 further comprising crimped, heat-resistant organic fibers compressed on the second side of the scrim, the fibers held in a compressed state by a thermoplastic binder.
4. The reinforced nonwoven fabric of claim 1 wherein the polymeric layer is a film.
5. The reinforced nonwoven fabric of claim 1 wherein the polymeric layer is a coating.
6. The reinforced nonwoven fabric of claim 1 wherein the polymeric layer comprises a polyurethane polymer.
7. The reinforced nonwoven fabric of claim 1 wherein the polymeric layer comprises a poly vinyl chloride polymer.
8. The reinforced nonwoven fabric of claim 1 wherein the polymeric layer has a thickness of 0.0005 to 0.003 inches.
9. The reinforced nonwoven fabric of claim 1 , wherein the heat-resistant organic fiber is a para-aramid fiber.
10. The reinforced nonwoven fabric of claim 9 , wherein the para-aramid fiber is poly(paraphenylene terephthalamide).
11. The reinforced nonwoven fabric of claim 1 , wherein the heat-resistant organic fiber is made from a polymer selected from the group consisting of polybenzazole, polybenzimidazole, and polyimide polymer.
12. The reinforced nonwoven fabric of claim 1 , wherein the heat-resistant organic fiber is a cellulose fiber that retains at least 10 percent of its fiber weight when heated in air to 700° C. at a rate of 20 degrees C. per minute.
13. The reinforced nonwoven fabric of claim 12 , wherein the cellulose fiber is a viscose fiber containing hydrated silicon dioxide in the form of a polysilicic acid with aluminum silicate sites.
14. The reinforced nonwoven fabric of claim 1 , wherein the heat-resistant organic fiber is blended with up to 50 weight percent modacrylic fibers.
15. The reinforced nonwoven fabric of claim 1 , wherein the thermoplastic binder comprises binder fiber.
16. The reinforced nonwoven fabric of claim 1 , wherein the thermoplastic binder comprises a combination of binder fiber and binder powder.
17. The reinforced nonwoven fabric of claim 1 wherein the open mesh scrim comprises thermoplastic material.
18. A fire blocked article comprising the reinforced nonwoven fabric of claim 1 .
19. A fire blocked mattress comprising the reinforced nonwoven fabric of claim 1 .
20. Fire blocked upholstered furniture comprising the reinforced nonwoven fabric of claim 1 .