Method for conditioning polyester and controlling expansion of polyester during thermoforming
A method for thermoforming a cellular thermoplastic resin comprises exposing a cellular thermoplastic resin to a controlled humidity environment to obtain a conditioned cellular thermoplastic resin, molding the conditioned cellular thermoplastic resin to form a desired shape, and heating the conditioned cellular thermoplastic resin to cause the crystalline content of the thermoplastic resin to be at least about 20-30 percent. A method for conditioning a cellular thermoplastic resin comprises exposing a cellular thermoplastic resin to a controlled humidity environment to obtain a conditioned cellular thermoplastic resin.
1 . A method for conditioning a cellular thermoplastic resin comprising exposing a cellular thermoplastic resin to a controlled humidity environment to obtain a conditioned cellular thermoplastic resin.
2 . A method for conditioning a cellular thermoplastic resin according to claim 1 , wherein the cellular thermoplastic resin is a polyester resin.
3 . A method for conditioning a cellular thermoplastic resin according to claim 1 , wherein the cellular thermoplastic resin is selected from the group consisting of polyethylene terephthalate, polyethylene naphthalate, polyethylene isophthalate, polybutylene terephthalate, polytrimethylene terephthalate and mixtures and copolymers thereof.
4 . A method for conditioning a cellular thermoplastic resin according to claim 1 , wherein the step of exposing a cellular thermoplastic resin to a controlled humidity environment comprises exposing the cellular thermoplastic resin to humidity level such that the final moisture level is at least about 0.34 percent by weight.
5 . A method for conditioning a cellular thermoplastic resin according to claim 1 , wherein the conditioned cellular thermoplastic resin has a moisture level of at least about 0.44 percent by weight.
6 . A method for conditioning a cellular thermoplastic resin according to claim 1 , wherein the conditioned cellular thermoplastic resin has a moisture level of at least about 0.55 percent by weight.
7 . A method for thermoforming a cellular thermoplastic resin, said method comprising:
exposing a cellular thermoplastic resin to a controlled humidity environment to obtain a conditioned cellular thermoplastic resin;
molding said conditioned cellular thermoplastic resin to form a desired shape; and
heating said conditioned cellular thermoplastic resin to cause the crystalline content of the thermoplastic resin to be at least about 20-30 percent.
8 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the cellular thermoplastic resin is a polyester resin.
9 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the cellular thermoplastic resin is selected from the group consisting of polyethylene terephthalate, polyethylene naphthalate, polyethylene isophthalate, polybutylene terephthalate, polytrimethylene terephthalate and mixtures and copolymers thereof.
10 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the step of exposing a cellular thermoplastic resin to a controlled humidity environment comprises exposing the cellular thermoplastic resin to humidity level of at least 25 percent relative humidity at a temperature of at least 32° C.
11 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the step of exposing a cellular thermoplastic resin to a controlled humidity environment comprises exposing the cellular thermoplastic resin to humidity level of at least 50 percent relative humidity at a temperature of at least 32° C.
12 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the conditioned cellular thermoplastic resin has a moisture level of at least about 0.34 percent by weight.
13 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the conditioned cellular thermoplastic resin has a moisture level of at least about 0.44 percent by weight.
14 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the conditioned cellular thermoplastic resin has a moisture level of at least about 0.5 percent by weight.
15 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the step of heating the cellular thermoplastic resin causes the crystalline content of the cellular thermoplastic resin to reach a predetermined level.
16 . A method for thermoforming a cellular thermoplastic resin according to claim 7 , wherein the step of heating the cellular thermoplastic resin causes the crystalline content of the cellular thermoplastic resin to be at least about 20 percent.
17 - 20 . (canceled)