Layered lithium-nickel-based compound oxide powder and its production process
View Patent ↗A layered lithium-nickel-based compound oxide powder for a positive electrode material for a high density lithium secondary cell, capable of providing a lithium secondary cell having a high capacity and excellent in the rate characteristics also, is provided. A layered lithium-nickel-based compound oxide powder for a positive electrode material for a lithium secondary cell, characterized in that the bulk density is at least 2.0 g/cc, the average primary particle size B is from 0.1 to 1 μm, the median diameter A of the secondary particles is from 9 to 20 μm, and the ratio A/B of the median diameter A of the secondary particles to the average primary particle size B, is within a range of from 10 to 200. In production of a layered lithium-nickel-based compound oxide powder, which comprises spray drying a slurry having a nickel compound and a transition metal element compound capable of substituting lithium other than nickel, dispersed in a liquid medium, followed by mixing with a lithium compound, and firing the mixture, the spray drying is carried out under conditions of 0.4≦G/S≦4 and G/S≦0.0012V, when the slurry viscosity at the time of the spray drying is represented by V (cp), the slurry supply amount is represented by S (g/min) and the gas supply amount is represented by G (L/min).
1. A layered lithium-nickel-based compound oxide powder for a positive electrode material for a lithium secondary cell, which is represented by the following formula (1), wherein:
said powder comprises secondary particles,
said secondary particles are agglomerates of primary particles,
said powder has a bulk density of at least 2.0 g/cc,
said primary particles have an average primary particle size B of from 0.1 to 1 μm,
said secondary particles have a median diameter A of from 9 to 20 μm, and
the ratio A/B of said median diameter A of said secondary particles to said average primary particle size B, is within a range of from 10 to 200:
Li 1+x Ni 1−y−z−p Mn y Co z M p O 2 (1)
wherein 0≦x≦0.20, 0.1≦y≦0.5, 0.1≦z≦0.5, 0≦p≦0.2, 0.2≦y+z+p≦0.8, and M is at least one member selected from the group consisting of Al, Fe, Ti, Mg, Cr, Ga, Cu, Zn, Nb and Zr.
2. The layered lithium-nickel-based compound oxide powder according to claim 1 , which has BET specific surface area of from 0.5 to 1 m 2 /g.
3. The layered lithium-nickel-based compound oxide powder according to claim 1 , wherein in formula (1), y is at least 0.2 and at most 0.4, z is at least 0.2 and at most 0.4, and y+z+p is at least 0.3 and at most 0.7.
4. The layered lithium-nickel-based compound oxide powder according to claim 1 , wherein in formula (1), x is at least 0.02 and at most 0.10.
5. A process for producing a layered lithium-nickel-based compound oxide powder for a positive electrode material for a lithium secondary cell according to claim 1 , which comprises spray drying a slurry having a nickel compound and a metal element compound capable of partially substituting nickel, dispersed in a liquid medium, followed by mixing with a lithium compound, and firing the mixture to produce a layered lithium-nickel-based compound oxide powder for a positive electrode material for a lithium secondary cell, characterized in that when the slurry viscosity at the time of the spray drying is represented by V (cp), the slurry supply amount is represented by S (g/min) and the gas supply amount is represented by G (L/min), the spray drying is carried out under such conditions that the gas/slurry ratio G/S is 0.4≦G/S≦4, and the relation between the slurry viscosity V and the gas/slurry ratio G/S is G/S≦0.0012V.
6. A layered lithium-nickel-based compound oxide powder for a positive electrode material for a lithium secondary cell, produced by the process for producing a layered lithium-nickel-based compound oxide powder as defined in claim 5 .
7. A positive electrode for a lithium secondary cell, characterized in that a positive electrode active material layer comprising a layered lithium-nickel-based compound oxide powder as defined in claim 1 and a binder are formed on a current collector.
8. A lithium secondary cell comprising a negative electrode capable of absorbing and desorbing lithium, a non-aqueous electrolyte containing a lithium salt and a positive electrode according to claim 7 .
9. The layered lithium-nickel-based compound oxide powder according to claim 6 , which has a BET specific surface area of from 0.5 to 1 m 2 /g.
10. The layered lithium-nickel-based compound oxide powder according to claim 6 , wherein in formula (1), y is at least 0.2 and at most 0.5, z is at least 0.1 and at most 0.4, and y+z+p is at least 0.2 and at most 0.7.
11. The layered lithium-nickel-based compound oxide powder according to claim 6 , wherein in formula (1), x is at least 0.01 and at most 0.15.
12. The positive electrode according to claim 7 , wherein said layered lithium-nickel-based compound oxide powder has a BET specific surface area of from 0.5 to 1 m 2 /g.
13. The positive electrode according to claim 7 , wherein in formula (1), y is at least 0.2 and at most 0.5, z is at least 0.1 and at most 0.4, and y+z+p is at least 0.2 and at most 0.7.
14. The positive electrode according to claim 7 , wherein in formula (1), x is at least 0.01 and at most 0.15.
15. The lithium secondary cell according to claim 8 , wherein said layered lithium-nickel-based compound oxide powder has a BET specific surface area is from 0.5 to 1 m 2 /g.
16. The lithium secondary cell according to claim 8 , wherein in formula (1), y is at least 0.2 and at most 0.5, z is at least 0.1 and at most 0.4, and y+z+p is at least 0.2 and at most 0.7.
17. The lithium secondary cell according to claim 8 , wherein in formula (1), x is at least 0.01 and at most 0.15.