Perpendicular magnetic recording medium
View Patent ↗There is provided a perpendicular magnetic recording medium according to which both the thermal stability of the magnetization is good and writing with a magnetic head is easy, and moreover the SNR is improved. In the case of a perpendicular magnetic recording medium comprising a nonmagnetic substrate 1 , and at least a nonmagnetic underlayer 2 , a magnetic recording layer 3 and a protective layer 4 formed in this order on the nonmagnetic substrate 1 , the magnetic recording layer 3 comprises a low K u region 31 layer having a perpendicular magnetic anisotropy constant (K u value) of not more than 1×10 5 erg/cm 3 , and a high K u region 32 layer having a K u value of at least 1×10 6 erg/cm 3 . Moreover, the magnetic recording layer 3 is made to have therein nonmagnetic grain boundaries that contain a nonmagnetic oxide and magnetically isolate crystal grains, which are made of a ferromagnetic metal, from one another.
1. A perpendicular magnetic recording medium, comprising a nonmagnetic substrate, a nonmagnetic underlayer, a magnetic recording layer and a protective layer formed in this order on said nonmagnetic substrate, wherein said magnetic recording layer comprises a low K u layer having a perpendicular magnetic anisotropy constant K u of not more than 1×10 5 erg/cm 3 , and a high K u layer having a perpendicular magnetic anisotropy constant K u of at least 1×10 6 erg/cm 3 .
2. The perpendicular magnetic recording medium according to claim 1 , wherein said high K u layer comprises an alloy thin film having Co as a principal component thereof with at least Pt added thereto and having a hexagonal close-packed crystal structure, and a preferred crystal orientation plane that is parallel to the film plane of said high K u layer is made to be the (002) plane.
3. The perpendicular magnetic recording medium according to claim 1 , wherein said high K u layer comprises a layered film in which layers of a Co alloy and an alloy having Pt or Pd as a principal component thereof each having a thickness of not more than 2 nm are formed alternately, and a preferred crystal orientation plane that is parallel to the film plane of said high K u layer is made to be the (111) plane.
4. The perpendicular magnetic recording medium according to claim 1 , wherein said high K u layer comprises crystal grains made of a ferromagnetic metal and nonmagnetic grain boundaries magnetically isolating said crystal grains from one another, and said nonmagnetic grain boundaries contain a nonmagnetic oxide as a principal component thereof.
5. The perpendicular magnetic recording medium according to claim 1 , wherein said low K u layer comprises a metal or alloy thin film having a face centered cubic crystal structure, and a preferred crystal orientation plane that is parallel to the film plane of said low K u layer is made to be the (111) plane.
6. The perpendicular magnetic recording medium according to claim 1 , wherein said low K u layer comprises crystal grains made of a ferromagnetic metal and nonmagnetic grain boundaries magnetically isolating said crystal grains from one another, and said nonmagnetic grain boundaries contain a nonmagnetic oxide as a principal component thereof.
7. The perpendicular magnetic recording medium according to claim 1 , wherein the ratio of the saturation magnetization M s of said low K u layer to the saturation magnetization M s of said high K u layer is in a range of 0.8 to 1.2.