Coating material composition

1. Coating materials comprising

I) one or more dispersions of hydroxyl-free polyurethanes and/or polyurethane-ureas (PU dispersions)

II) one or more aqueous solutions or dispersions of ionically modified, hydroxyl-containing polyurethanes and/or polyurethane-ureas, other than the constituents of component I), and

III) at least one crosslinker and

IV) optionally other film-forming resins, wherein the PU dispersions used in I) are obtained by

A) preparing an NCO-containing polyurethane prepolymer by reacting

A1) polyisocyanates with

A2) polymeric polyols and/or polyamines having number average molecular weights of 400 to 8000 g/mol,

A3) optionally low molecular weight compounds having number-average molecular weights of 17 to 400 g/mol selected from the group consisting of mono- and polyalcohols, mono- and polyamines and also amino alcohols,

A4) optionally isocyanate-reactive, ionically or potentially ionically hydrophilicizing compounds and/or

A5) optionally isocyanate-reactive nonionically hydrophilicizing compounds

A6) optionally in aliphatic ketones as solvents with the proviso that none of components A1) to A5) contains primary or secondary amino groups,

B) either dissolving the prepolymer obtained from step A) in aliphatic ketones or, diluting the prepolymer solution if the preparation has already been carried out in the presence of A6) by further addition of aliphatic ketones, and

C) reacting the remaining free NCO groups of the prepolymer with a chain extender component comprising

C1) hydrazine and/or hydrazine hydrate and

C2) optionally compounds meeting the definition of components A2), A3), A4) and/or A5),

with the proviso that

the compounds of component C2) contain primary and/or secondary amino groups,

the total amounts of C1) and C2) are such that an arithmetic degree of chain extension of 101 to 150% is attained and

the proportion of C1) and C2) is such that at least 40% of the free isocyanate groups are terminated by and/or chain-extended with amino groups from component C1)

at least one of A4) and A5) is utilized to prepare the NCO-containing polyurethane prepolymer A.

2. The coating materials according to claim 1 , wherein the PU dispersions prepared in step B) and optionally step A) use acetone or butanone as solvent.

3. The coating materials according to claim 1 , wherein the PU dispersions comprise the reaction product of 8 to 27% by weight of component A1), 65 to 85% by weight of component A2), 0 to 8% by weight of component A3), 0 to 10% by weight of component A4), 0 to 15% by weight of component A5), 1.0 to 2.5% by weight of C1) (based on pure hydrazine, N2H4) and 0 to 8% by weight of C2) in steps A) to C), the sum of A4) and A5) being 0.1 to 25% by weight and the sum of the components adding to 100% by weight.

4. The coating materials according to claim 1 , wherein polyisocyanates are used as crosslinkers in III).

5. The coating materials according to claim 4 , wherein the ratio of NCO groups of component III) to the OH groups of components II) and IV) is from 1.0:1.0 to 2.5:1.0.

6. The coating materials according to claim 1 , wherein the mixture of components I), II) and IV) contains 25 to 75% by weight of component II) and the amounts of I) and IV) are chosen such that the total amounts of I), II) and IV) add up to 100% by weight.

7. A method of making a coating comprising combining the coating materials according to claim 1 with one or more additives selected from the group consisting of defoamers, thickeners, pigments, dispersing assistants, matting agents, catalysts, anti-skinning agents, anti-settling agents, emulsifiers, additives which enhance the soft feel effect, and combinations thereof.

8. Coatings produced using coating materials according to claim 1 .

9. Substrates coated with coatings according to claim 8 .

10. The coating materials according to claim 2 , wherein the PU dispersions comprise the reaction product of 8 to 27% by weight of component A1), 65 to 85% by weight of component A2), 0 to 8% by weight of component A3), 0 to 10% by weight of component A4), 0 to 15% by weight of component A5), 1.0 to 2.5% by weight of C1) (based on pure hydrazine, N2H4) and 0 to 8% by weight of C2) in steps A) to C), the sum of A4) and A5) being 0.1 to 25% by weight and the sum of the components adding to 100% by weight.

11. The coating materials according to claim 2 , wherein polyisocyanates are used as crosslinkers in III).

12. The coating materials according to claim 11 , wherein the ratio of NCO groups of component III) to the OH groups of components II) and IV) is from 1.0:1.0 to 2.5:1.0.

13. Coatings produced using coating materials according to claim 2 .

14. Substrates coated with coatings according to claim 1 .

15. The coating materials according to claim 3 , wherein polyisocyanates are used as crosslinkers in III).

16. The coating materials according to claim 15 , wherein the ratio of NCO groups of component III) to the OH groups of components II) and IV) is from 1.0:1.0 to 2.5:1.0.

17. Coatings produced using coating materials according to claim 3 .

18. Substrates coated with coatings according to claim 17 .