Composite fiber cement article with radiation curable component
A composite building article is configured with one or more subsurface interfacial zones provided to improve the durability of the article. Each subsurface interfacial zone is made of a matrix of fiber cement and radiation curable material. The radiation curable material forms an interlocking network with the fiber cement to provide a interfacial zone against ingress of environmental agents that can degrade the article. The number, configuration and distribution of the subsurface interfacial zones can vary dependent on the desired characteristics of the final product. The subsurface interfacial zones also improves the adhesion between exterior coatings and the substrate as the interfacial zones can be integrally formed with the substrate as well as exterior coating layer.
1. A composite building article having a first zone comprises a fiber cement substrate having a porosity of between about 20%-40% by volume which comprises predominantly fiber cement comprising
about 20-60 weight % cement;
about 0 to 60 weight % silica;
about 0.1 to 15 weight % cellulose fiber; and
about 0-5 weight % of at least one additive;
a second zone which comprises predominantly an EB curable urethane acrylate resin having a solids content of at least 80%, and a subsurface interfacial zone interposed therebetween, the subsurface interfacial zone comprising an interlocking matrix formed of the EB curable urethane acrylate resin and the fiber cement, wherein said interfacial zone is integrally formed with the first and second zones and configured to increase durability of the building article.
2. The composite building article of claim 1 , wherein the subsurface interfacial zone contains substantially no catalyst.
3. The composite building article of claim 1 , wherein the thickness of the subsurface interfacial zone is controlled by modifying a characteristic selected from the group consisting of the porosity of the first zone, viscosity of the radiation curable component, and combinations thereof.
4. The composite building article of claim 1 , wherein the subsurface interfacial zone has a thickness of about 1 μm-1,000 μm.
5. The composite building article of claim 1 , wherein the composite building article is selected from the group consisting of cladding panels, sheets, boards, planks, trims, shakes, and pipes.
6. The composite building article of claim 1 , wherein the cement is in the range of about 23.5 to 26.5% of the composition.
7. The composite building article of claim 1 , wherein cellulose fibers comprises about 7-9% of the composition.
8. The composite building article of claim 1 , wherein the cellulose fibers are unbleached.
9. The composite building article of claim 8 , wherein the unbleached cellulose fibers comprise about 11% by weight of the composition.
10. The composite building article of claim 1 , wherein the EB curable urethane acrylate resin consists essentially of about 45% difunctional polyester acrylate, about 15% metal acrylate, and about 15% 1,6 hexanediol diacrylate.
11. The composite building article of claim 10 , wherein the subsurface interfacial zone is approximately 5 μm to 20 μm.
12. The composite building article of claim 1 , wherein the EB curable urethane acrylate resin consists essentially of about 20% hexafunctional aliphatic urethane acrylate, 14% trifunctional polyester acrylate, and about 14% 3-mercaptopropinoate.
13. The composite building article of claim 12 , wherein the subsurface interfacial zone is approximately 5 μm to 20 μm.
14. A composite building article having a first zone consisting essentially of:
a fiber cement composition consisting essentially of:
20-60 weight % cement;
0 to 60 weight % silica;
0.1 to 15 weight % unbleached cellulose fiber; and
0-5 weight % of at least one additive;
a second zone which comprises predominantly an EB curable urethane acrylate resin; and
a subsurface interfacial zone interposed and integrally formed with the first and second zones and comprising an interlocking matrix formed of the EB curable urethane acrylate resin and the fiber cement, the first zone having a porosity of between about 20%-40% by volume and the EB curable urethane acrylate resin in the subsurface interfacial zone contains substantially no catalyst and is curable primarily by radiation.
15. The composite building article of claim 14 , wherein cellulose fibers comprises about 7-9% of the composition.
16. The composite building article of claim 14 , wherein the unbleached cellulose fibers comprise about 11% by weight of the composition.
17. The composite building article of claim 14 , wherein the at least one additive is selected from the group consisting of flow additive, dispersant, thixotrope, defoamer, and a combination thereof.