Magnetic recording medium
View Patent ↗A magnetic recording medium including a polymer support having thereon at least one magnetic layer containing a ferromagnetic metal powder having an average major axis length of from 20 to 100 nm or a ferromagnetic hexagonal ferrite powder having an average tabular diameter of from 5 to 40 nm and a binder, the polymer support having an intrinsic viscosity of from 0.47 to 0.51 dL/g, a Young's modulus in the machine direction of from 7.0 to 8.6 GPa, a Young's modulus in the transverse direction of from 5.4 to 8.0 GPa, and a breaking strength in the transverse direction of from 370 to 450 MPa.
1. A magnetic recording medium comprising: a polymer support; and at least one magnetic layer containing a binder and one of a ferromagnetic metal powder having an average major-axis length of from 20 to 100 nm and a ferromagnetic hexagonal ferrite powder having an average tabular diameter of from 5 to 40 nm,
wherein the polymer support has an intrinsic viscosity of from 0.47 to 0.51 dL/g, a Young's modulus in a machine direction of from 7.0 to 8.6 GPa, a Young's modulus in a transverse direction of from 5.4 to 8.0 GPa, and a breaking strength in the transverse direction of from 370 to 450 MPa.
2. The magnetic recording medium according to claim 1 , wherein:
the polymer support is a laminated polyester film having a thickness of not more than 8 μm and comprising at least a first layer and a second layer;
the first layer is provided at one side where the magnetic layer is formed, and has a first contact stylus three-dimensional surface roughness of from 1 to 6 nm;
the second layer is provided at opposite side, and has a second contact stylus three-dimensional surface roughness of 6 to 10 nm; and
the first contact stylus three-dimensional surface is smaller than the second contact stylus three-dimensional surface roughness.
3. The magnetic recording medium according to claim 1 , wherein the intrinsic viscosity is from 0.47 to 0.50 dL/g.
4. The magnetic recording medium according to claim 1 , wherein the Young's modulus in a machine direction is from 7.0 to 8.5 GPa, and the Young's modulus in a transverse direction is 5.6 to 7.8 Gpa.
5. The magnetic recording medium according to claim 2 , wherein the first contact stylus three-dimensional surface is from 1.5 to 5.5 nm, and the second contact stylus three-dimensional surface roughness is from 6.5 to 9.0.
6. The magnetic recording medium according to claim 2 , wherein the first layer contains a fine grain having an average diameter of from 30 to 150 nm at a ratio of not more than 0.1% by weight.
7. The magnetic recording medium according to claim 6 , wherein the fine grain is selected from at least one of silica, calcium carbonate, alumina, a polyacrylic grain, and a polystyrene grain.
8. A magnetic recording medium comprising: a polymer support; and at least one magnetic layer containing a binder and one of a ferromagnetic metal powder having an average major-axis length of from 20 to 100 nm and a ferromagnetic hexagonal ferrite powder having an average tabular diameter of from 5 to 40 nm,
wherein the polymer support has a number average molecular weight of from 12,000 to 18,000, a weight average molecular weight of from 32,000 to 40,000, a Young's modulus in a machine direction of from 7.0 to 8.6 GPa, and a Young's modulus in a transverse direction of from 5.4 to 8.0 GPa.
9. The magnetic recording medium according to claim 8 , wherein:
the polymer support is a laminated polyester film having a thickness of not more than 8 μm and comprising at least a first layer and a second layer;
the first layer is provided at one side where the magnetic layer is formed, and has a first contact stylus three-dimensional surface roughness of from 1 to 6 nm;
the second layer is provided at opposite side, and has a second contact stylus three-dimensional surface roughness of 6 to 10 nm; and
the first contact stylus three-dimensional surface is smaller than the second contact stylus three-dimensional surface roughness.
10. The magnetic recording medium according to claim 8 , wherein the number average molecular weight is from 14,000 to 17,000, and the weight average molecular weight is from 33,000 to 38,000.
11. The magnetic recording medium according to claim 8 , wherein the Young's modulus in a machine direction is from 7.0 to 8.5 GPa, and the Young's modulus in a transverse direction is 5.6 to 7.8 Gpa.
12. The magnetic recording medium according to claim 9 , wherein the first contact stylus three-dimensional surface is from 1.5 to 5.5 nm, and the second contact stylus three-dimensional surface roughness is from 6.5 to 9.0.
13. The magnetic recording medium according to claim 9 , wherein the second layer contains a fine grain having an average diameter of from 80 to 800 nm at a ratio of from 0.08 to 0.8% by weight.
14. The magnetic recording medium according to claim 13 , wherein the fine grain is selected from at least one of calcium carbonate, silica, alumina, a polystyrene grain, and a silicone resin grain.
15. A magnetic recording medium comprising: a polymer support; and at least one magnetic layer containing a binder and one of a ferromagnetic metal powder having an average major-axis length of from 20 to 100 nm and a ferromagnetic hexagonal ferrite powder having an average tabular diameter of from 5 to 40 nm,
wherein the polymer support has an intrinsic viscosity of from 0.47 to 0.50 dL/g, a number average molecular weight of from 12,000 to 18,000, a weight average molecular weight of from 32,000 to 40,000, a Young's modulus in a machine direction of from 7.0 to 8.6 GPa, a Young's modulus in a transverse direction of from 5.4 to 8.0 GPa, and a breaking strength in the transverse direction of from 370 to 450 MPa.