Lead-free glass tubing, especially for encapsulating diodes and diodes encapsulated with same
View Patent ↗The lead-free glass tubing of the SiO 2 —B 2 O 3 —R 2 O—BaO—ZnO—TiO 2 system has a composition, in percent by weight on an oxide basis, consisting essentially of: SiO 2 , 34 to 52; B 2 O 3 , 10 to 25; Al 2 O 3 , 0 to 25; Li 2 O, 2 to 6; Na 2 O, 4 to 10; K 2 O, 2 to 6; CaO, 0 to 4; BaO, 1 to 5; ZnO, 4 to 12; TiO 2 , 2 to 6, and at least one refining agent in an effective amount for refining. An encapsulated diode consisting of a diode encapsulated with this lead-free glass tubing is also disclosed.
1. Lead-free glass tubing having a composition, in percent by weight on an oxide basis, consisting essentially of:
SiO 2
34 to 52,
B 2 O 3
10 to 25,
Al 2 O 3
0 to 25,
Li 2 O
2 to 6,
Na 2 O
4 to 10,
K 2 O
2 to 6,
CaO
0 to 4,
BaO
1 to 5,
ZnO
4 to 12,
TiO 2
2 to 6, and
at least one refining agent in an effective amount
for refining.
at least one refining agent in an effective amount for refining.
2. The lead-free glass tubing as defined in claim 1 , wherein said at least one refining agent is selected from the group consisting of Sb 2 O 3 , As 2 O 3 , CeO 2 and NaCl.
3. An encapsulated diode comprising a diode and lead-free glass tubing encapsulating said diode, wherein said lead-free glass tubing has a composition, in percent by weight on an oxide basis, consisting essentially of:
SiO 2
34 to 52,
B 2 O 3
10 to 25,
Al 2 O 3
0 to 25,
Li 2 O
2 to 6,
Na 2 O
4 to 10,
K 2 O
2 to 6,
CaO
0 to 4,
BaO
1 to 5,
ZnO
4 to 12,
TiO 2
2 to 6, and
at least one refining agent in an effective amount
for refining.
at least one refining agent in an effective amount for refining.
4. The encapsulated diode as defined in claim 3 , wherein said at least one refining agent is selected from the group consisting of Sb 2 O 3 , As 2 O 3 , CeO 2 and NaCl.
5. The lead-free glass tubing as defined in claim 1 , wherein said composition consists essential of from 38 to 50 percent by weight of said SiO 2 , from 11 to 21 percent by weight of said B 2 O 3 , from 1 to 22 percent by weight of said Al 2 O 3 , from 3 to 5 percent by weight of said Li 2 O, from 5 to 9 percent by weight of said Na 2 O, from 3 to 5 percent by weight of said K 2 O, from 1 to 2 percent by weight of said CaO, from 1 to 3 percent by weight of said BaO, from 6 to 12 percent by weight of said ZnO and from 3 to 5 percent by weight of said TiO 2 .
6. The lead-free glass tubing as defined in claim 1 , wherein said composition consists essential of from 38 to 47 percent by weight of said SiO 2 , from 13 to 21 percent by weight of said B 2 O 3 , from 2 to 20 percent by weight of said Al 2 O 3 , from 3 to 5 percent by weight of said Li 2 O, from 5 to 8 percent by weight of said Na 2 O, from 3 to 5 percent by weight of said K 2 O, from 1 to 2 percent by weight of said CaO, from 1 to 3 percent by weight of said BaO, from 6 to 10 percent by weight of said ZnO and from 3 to 5 percent by weight of said TiO 2 .
7. The lead-free glass tubing as defined in claim 1 , having a processing temperature V A ≦850° C., an upper devitrificatian temperature OEG of 690°, a softening temperature E W ≦600° C., a transformation temperature Tg≦480° C., a thermal expansion coefficient α 20/300 of 8.6×10 −6 /K to 9.2×10 −6 /K and an elastic modulus E>50 Gpa.