Fluoropolymer emulsion coatings
View Patent ↗The present invention relates to an aqueous/oil emulsion containing fluoropolymer that is capable of forming thick coatings in a single pass, which coatings after drying and baking are free of cracks.
1. An aqueous and oil emulsion containing particles of fluoropolymer, wherein said fluoropolymer comprises 10-90 wt% of the emulsion and wherein said fluoropolymer particles comprise a first group of particles having an average particle size of less than 1 micrometer and a second group of particles having an average particle size of 20-100 micrometers, and wherein the oil component of the emulsion is an aliphatic or aromatic hydrocarbon that is immiscible with water at room temperature, 15-25° C., and the oil does not exceed 5 weight % based on the weight of the emulsion, and further wherein the emulsion has a viscosity of at least 2000 centipoises.
2. The emulsion of claim 1 wherein said fluoropolymer particles comprise tetrafluoroethylene/hexafluoropropylene copolymer, tetrafluoroethylene/perfluoro(alkyl vinyl ether) copolymer or polytetrafluoroethylene.
3. The emulsion of claim 1 wherein said oil is aromatic hydrocarbon oil.
4. The emulsion of claim 1 containing emulsifying agent.
5. The emulsion of claim 4 wherein said emulsifying agent is an aliphatic hydrocarbon alcohol containing at least 8 carbon atoms.
6. An aqueous and oil emulsion containing particles of fluoropolymer and an emulsifying agent, wherein said fluoropolymer comprises 10-90 wt% of the emulsion, said emulsifying agent is an aliphatic hydrocarbon alcohol containing at least 8 carbon atoms, and said emulsion has a viscosity of at least 2000 centipoises, and further wherein the oil component of the emulsion is an aliphatic or aromatic hydrocarbon that is immiscible with water at room temperature, 15-25° C., and the oil does not exceed 5 weight % based on the weight of the emulsion.