Polyvinylbutyral rolls having thick edges relative to the interior of the roll and a process for preparing same
View Patent ↗The present invention is an extruded sheet of polyvinylbutyral having thick edges relative to the interior region, whereby the sheet can be taken up on a roll and aged in such a manner that the roll attains a cylindrical shape due to loss of circumference of the roll edge during aging.
1. A process for producing cylindrical-shaped polyvinyl butyral interlayer rolls comprising the steps: (a) extruding a polyvinyl butyral interlayer sheet such that the extreme edges of the polyvinyl butyral interlayer sheet are thicker than the middle section of the polyvinyl butyral interlayer sheet; (b) forming a roll from the extruded polyvinyl butyral interlayer sheet by taking up the extruded polyvinyl butyral interlayer sheet onto a wind-up roll such that the edges of the roll initially have a larger circumference than the middle of the roll; (c) allowing the polyvinyl butyral interlayer roll to remain on the wind-up roll for a time sufficient for the circumference of the polyvinyl butyral interlayer roll at the edges to be within 10% of the circumference of the middle of the polyvinyl butyral interlayer roll.
2. The process of claim 1 further comprising roughening the surface of the polyvinyl butyral interlayer sheet prior to the forming the roll.
3. The process of claim 2 wherein the roughening comprises mechanically embossing the interlayer sheet followed by quenching.
4. The process of claim 3 further comprising forming a pre-laminate from the polyvinyl butyral interlayer and at least one ply of glass and laminating the pre-laminate to form a glass laminate, including a de-airing step comprising removing air and trapped gasses from the pre-laminate structure before or during the lamination, and wherein the polyvinyl butyral interlayer sheet is plasticized with a plasticizer selected from the group consisting of triethyleneglycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, triethylene glycol di-2-ethylbutyrate, and triethylene glycol di-2-ethylhexanoate.
5. The process of claim 3 further comprising forming a pre-laminate from the polyvinyl butyral interlayer and at least one ply of glass and laminating the pre-laminate to form a glass laminate, including a de-airing step comprising removing air and trapped gasses from the pre-laminate structure before or during the lamination, wherein the polyvinyl butyral interlayer sheet is plasticized with a plasticizer selected from the group consisting of triethyleneglycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, triethylene glycol di-2-ethylbutyrate, and triethylene glycol di-2-ethylhexanoate, and wherein the polyvinyl butyral interlayer sheet contains as an adhesion control agent, an alkali or alkaline earth metal carboxylate.
6. The process of claim 2 wherein the roughening comprises melt fracture during extrusion of the interlayer sheet followed by quenching.
7. The process of claim 6 further comprising forming a pre-laminate from the polyvinyl butyral interlayer and at least one ply of glass and laminating the pre-laminate to form a glass laminate, including a de-airing step comprising removing air and trapped gasses from the pre-laminate structure before or during the lamination, and wherein the polyvinyl butyral interlayer sheet is plasticized with a plasticizer selected from the group consisting of triethyleneglycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, triethylene glycol di-2-ethylbutyrate, and triethylene glycol di-2-ethylhexanoate.
8. The process of claim 6 further comprising forming a pre-laminate from the polyvinyl butyral interlayer and at least one ply of glass and laminating the pre-laminate to form a glass laminate, including a de-airing step comprising removing air and trapped gasses from the pre-laminate structure before or during the lamination, wherein the polyvinyl butyral interlayer sheet is plasticized with a plasticizer selected from the group consisting of triethyleneglycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, triethylene glycol di-2-ethylbutyrate, and triethylene glycol di-2-ethylhexanoate, and wherein the polyvinyl butyral interlayer sheet contains as an adhesion control agent, an alkali or alkaline earth metal carboxylate.
9. The process of claim 2 wherein the polyvinyl butyral interlayer sheet is plasticized with a plasticizer selected from the group consisting of triethyleneglycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, triethylene glycol di-2-ethylbutyrate, and triethylene glycol di-2-ethylhexanoate.
10. The process of claim 9 wherein the polyvinyl butyral interlayer sheet contains as an adhesion control agent, an alkali or alkaline earth metal carboxylate.
11. The process of claim 10 further comprising forming a pre-laminate from the polyvinyl butyral interlayer and at least one ply of glass and laminating the pre-laminate to form a glass laminate, including a de-airing step comprising removing air and trapped gasses from the pre-laminate structure before or during the lamination.
12. The process of claim 9 further comprising forming a pre-laminate from the polyvinyl butyral interlayer and at least one ply of glass and laminating the pre-aminate to form a glass laminate, including a de-airing step comprising removing air and trapped gasses from the pre-laminate structure before or during the lamination.
13. The process of claim 2 wherein the polyvinyl butyral interlayer sheet is plasticized with triethylene glycol di-2-ethyl hexanoate.
14. The process of claim 2 wherein the polyvinyl butyral interlayer sheet contains as an adhesion control agent, an alkali or alkaline earth metal carboxylate.
15. The process of claim 2 further comprising forming a pre-laminate from the polyvinyl butyral interlayer and at least one ply of glass and laminating the pre-laminate to form a glass laminate, including a de-airing step comprising removing air and trapped gasses from the pre-laminate structure before or during the lamination.
16. The process of claim 1 wherein the polyvinyl butyral interlayer sheet is plasticized with a plasticizer selected from the group consisting of triethyleneglycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, triethylene glycol di-2-ethylbutyrate, and triethylene glycol di-2-ethylhexanoate.
17. The process of claim 1 wherein the polyvinyl butyral interlayer sheet is plasticized with triethylene glycol di-2-ethyl hexanoate.
18. The process of claim 1 wherein the polyvinyl butyral interlayer sheet contains as an adhesion control agent, an alkali or alkaline earth metal carboxylate.
19. The process of claim 1 further comprising forming a glass laminate from the polyvinyl butyral interlayer and at least one ply of glass.
20. The process of claim 1 further comprising forming a pre-laminate from the polyvinyl butyral interlayer and at least one ply of glass and laminating the pre-laminate to form a glass laminate, including a de-airing step comprising removing air and trapped gasses from the pre-laminate structure before or during the lamination.