Method of measuring the adhesion of a coating to a substrate
View Patent ↗A method of measuring the adhesion of a coating to a substrate, wherein the measurement is done in air and wherein an ultrasound transducer is applied to the substrate by means of a thin film of gel, and a quality factor is calculated, given by the ratio between the amplitudes of the echoes associated with the first two reflections on the substrate/coating interface after passing through the substrate or on the coating/air interface after passing through the substrate and the coating.
1. A method of measuring the adhesion of a coating to a substrate, consisting in sending ultrasound waves by means of a transducer toward the substrate and the coating, picking up a series of echoes resulting from reflections of the ultrasound waves on the surfaces of the substrate and of the coating, and calculating an amplitude ratio of two successive echoes, wherein the measurement is done in air and wherein the method also consists in applying the transducer to the substrate by means of a thin film of gel, calculating a coating quality factor given by the ratio between the amplitudes of the echoes associated with the first two reflections on the substrate/coating interface after passing through the substrate or on the coating/air interface after passing through the substrate and the coating, and in determining the adhesion of the coating from a correlation function between the quality factor and the breaking stress of the coating, obtained previously by mechanical tests on calibration test pieces.
2. The method as claimed in claim 1 , wherein the ultrasound waves have a frequency of approximately 5 to 10 megahertz.
3. The method as claimed in claim 1 , wherein the quality factor measurements are carried out in situ on coated parts.
4. The method as claimed in claim 3 , which consists in repeating the measurements on the parts at regular or irregular time intervals to monitor the trend of the quality of the adhesion of the coating to the parts over time.
5. The method as claimed in claim 1 , wherein the coating and the substrate are metallic.
6. The method as claimed in claim 1 , wherein the thin film of gel has a thickness of approximately 10 μm.
7. The method as claimed in claim 1 , wherein the quality factor of the coating given by the ratio between the amplitudes of the echoes associated with the first two reflections on the substrate/coating interface after passing through the substrate is expressed as:
Q
′
=
ⅇ
2
α
1
x
1
r
1
cc
·
1
r
12
in which α 1 is the attenuation coefficient of the ultrasound waves in the substrate, x 1 is the thickness of the substrate, and r 1cc and r 12 are amplitude-wise reflection coefficients at the substrate/thin film interface and at the substrate/coating interface, respectively.
8. The method as claimed in claim 1 , wherein the quality factor of the coating given by the ratio between the amplitudes of the echoes associated with the first two reflections on the coating/air interface after passing through the substrate and the coating is expressed as:
Q
=
ⅇ
2
α
1
x
1
r
1
cc
·
ⅇ
2
α
2
x
2
t
12
t
21
in which α 1 and α 2 are the attenuation coefficients of the ultrasound waves in the substrate and in the coating, respectively, x 1 and x 2 are the thicknesses of the substrate and of the coating, respectively, t 12 and t 21 are the amplitude transmission coefficients from the substrate to the coating and from the coating to the substrate, respectively, and r 1cc is the amplitude-wise reflection coefficient at the substrate/thin film interface.