Heat-resistant, paintable two-sided acrylic-based adhesive tape
View Patent ↗A heat-resistant, paintable two-sided acrylic-based adhesive tape and method for adhering the tape to two substrates is provided. The tape is comprised of a solid acrylic-based carrier including an acrylic-based adhesive on both sides of the carrier. The carrier preferably includes polymeric microspheres to impart compressibility to the tape. The tape includes a conformable, heat resistant polyolefin-based release liner. In use, the tape is adhered on one side to a first substrate, the liner is removed, and the tape is adhered on the other side to a second substrate. The two substrates with the tape are then exposed to elevated temperatures such as those encountered in an automotive, appliance, or other commercial paint bake process. The tape can withstand temperatures up to 300° F. and can be painted without degradation of the adhesive and without a reduction of the adhesive properties of the tape.
1. A conformable, heat resistant two-sided acrylic-based tape comprising:
a solid acrylic-based carrier having first and second sides, and including pre-expanded polymeric microspheres;
an acrylic-based adhesive on both side of said carrier; and
a conformable heat resistant removable liner comprised of a polyolefin-based material adhered by said adhesive to at least one side of said carrier; and
wherein said tape withstands temperatures up to 300° F.
2. The tape of claim 1 having a thickness of about 0.5 to 2.0 mm.
3. The tape of claim 1 having a peel strength of at least 20 N/cm after being processed through one paint bake cycle.
4. The tape of claim 1 wherein said pre-expanded polymeric microspheres have a diameter ranging from about 65 to 135 microns.
5. The tape of claim 1 wherein said pre-expanded polymeric microspheres have a concentration of about 4% by weight of the carrier.
6. The tape of claim 1 wherein said pre-expanded polymeric microspheres are heat resistant up to at least a temperature of 300° F.
7. The tape of claim 1 wherein said pre-expanded polymeric microspheres are hollow.
8. The tape of claim 1 wherein said microspheres have a concentration of about 4% by weight of the carrier.