Multilayer polyethylene thin films
A multilayer thin film is disclosed. The multilayer thin film has a thickness within the range of about 0.1 mil to about 1 mil and comprises at least one layer of a linear low density polyethylene (LLDPE) and at least one layer of a high density polyethylene (HDPE) or a medium density polyethylene (MDPE). The multilayer thin film has high tear strength and an excellent combination of other properties.
1 . A multilayer thin film having a thickness within the range of about 0.1 mil to about 1 mil, comprising at least one layer of a linear low density polyethylene (LLDPE) and at least one layer of a high density polyethylene (HDPE) or a medium density polyethylene (MDPE), and having a normalized machine-direction tear strength of 44 grams/mil or greater
2 . The multilayer thin film of claim 1 which has a thickness within the range of about 0.4 mil to about 0.8 mil.
3 . The multilayer thin film of claim 1 which has a thickness within the range of about 0.5 mil to about 0.8 mil.
4 . The multilayer thin film of claim 1 said film being oriented in the machine direction.
5 . The multilayer thin film of claim 1 is an HDPE/LLDPE/HDPE three-layer film.
6 . The multilayer thin film of claim 5 which has a normalized machine-direction tear strength greater than 150 grams/mil.
7 . The multilayer thin film of claim 5 which has a normalized machine-direction tear strength greater than 200 grams/mil.
8 . The multilayer thin film of claim 5 which is oriented in the machine direction with a drawdown ratio within the range of about 3 to about 6.
9 . The multilayer thin film of claim 8 wherein the drawdown ratio is within the range of about 4 to about 6.
10 . The multilayer thin film of claim 5 wherein each HDPE has a density, the same or different, within the range of 0.945 to 0.965 g/cm 3 and the LLDPE has a density within the range of 0.865 to 0.925 g/cm 3 .
11 . The multilayer thin film of claim 5 wherein the LLDPE and each HDPE have weight average molecular weights, the same or different, within the range of 120,000 to 1,000,000 and number average molecular weights, the same or different, within the range of 10,000 to 500,000.
12 . The multilayer thin film of claim 5 which has a thickness within the range of about 0.4 to 0.8 mil, a normalized machine-direction tear strength greater than 44 grams/mil, a machine-direction tensile strength at yield greater than 4,000 psi, a machine-direction tensile strength at break greater than 9,000 psi, a 1% secant machine-direction modulus greater than 150,000 psi, a dart-drop strength greater than 50 grams, a 1% secant transverse-direction modulus greater than 150,000 psi, a haze less than 60%, and a gloss greater than 20.
13 . The multilayer thin film of claim 1 which is an MDPE/LLDPE/MDPE three-layer film.
14 . The multilayer thin film of claim 13 which has a normalized machine-direction tear strength greater than 150 grams/mil.
15 . The multilayer thin film of claim 13 which has a normalized machine-direction tear strength greater than 200 grams.
16 . The multilayer thin film of claim 13 which is oriented in the machine direction with a drawdown ratio within the range of about 2 to about 6.
17 . The multilayer thin film of claim 16 wherein the drawdown ratio is within the range of about 2 to about 4.
18 . The multilayer thin film of claim 13 wherein each MDPE has a density, the same or different, within the range of 0.930 to 0.940 g/cm 3 and the LLDPE has a density within the range of 0.865 to 0.925 g/cm 3 .
19 . The multilayer thin film of claim 13 wherein the LLDPE and each MDPE, the same or different, have weight average molecular weights within the range of 120,000 to 1,000,000 and number average molecular weights, the same or different, within the range of 10,000 to 500,000.
20 . A multilayer thin film of claim 13 which has a thickness within the range of about 0.4 to 0.8 mil, a normalized machine-direction tear strength greater than 44 grams/mil, a machine-direction tensile strength at yield greater than 4,000 psi, a machine-direction tensile strength at break greater than 9,000 psi, a 1% secant machine-direction modulus greater than 150,000 psi, a dart-drop strength greater than 50 grams, a 1% secant transverse-direction modulus greater than 150,000 psi, a haze less than 60%, and a gloss greater than 20.