Method of making ceramic component containing inclusions
View Patent ↗A ceramic component is disclosed, including a sintered ceramic body from a composition comprising a first ceramic material, and a plurality of inclusions in the ceramic body, each inclusion comprising graphite and a second material.
1. A method for forming a ceramic component, comprising:
providing particles of a first ceramic material;
granulating particles of graphite and particles of a second ceramic material to form granules containing graphite and second ceramic material;
mixing the granules with the particles of the first ceramic material to form a mixture, wherein the granules comprise a different material as compared to the particles of the first ceramic material, and wherein mixing the granules and the particles of the first ceramic material is performed after granulating the particles of graphite and the particles of the second ceramic material;
forming a shaped body from the mixture; and
sintering the shaped body.
2. The method of claim 1 , wherein granulating is carried out by casting or by spray tying.
3. The method of claim 2 , wherein granulating is carried out by spray drying.
4. The method of claim 1 , wherein the mixture is in the form of a slurry, and further comprising a step of granulating the slurry to form a granulated product for forming the shaped body.
5. The method of claim 1 , wherein the granules comprise about 5 to about 65 wt % of said second ceramic material.
6. The method of claim 1 , wherein the granules have an average size within a range of about 10 microns to about 400 microns.
7. The method of claim 1 , wherein the shaped body is formed by pressing.
8. The method of claim 1 , wherein sintering is carried out by a pressureless sintering.
9. The method of claim 1 , wherein the particles of the first ceramic material comprises SiC.
10. The method of claim 9 , wherein the particles of the first ceramic material comprises alpha SiC, beta SiC, or a combination of alpha SiC and beta SiC.
11. The method of claim 1 , wherein the first and second ceramic materials are the same material.
12. The method of claim 9 , wherein the particles of the first ceramic material consist essentially of SiC.
13. The method of claim 1 , further comprising adding a fluid to the granules after granulating the particles of graphite and the particles of the second ceramic material, and before forming the shaped body.
14. A method for forming a ceramic component, comprising:
providing particles of a first ceramic material, wherein the particles of the first ceramic material are substantially free of graphite;
granulating particles of graphite and particles of a second ceramic material to form granules containing graphite and second ceramic material;
mixing the granules with the particles of the first ceramic material to form a mixture, wherein mixing the granules and the particles of the first ceramic material is performed after granulating the particles of graphite and the particles of the second ceramic material;
forming a shaped body from the mixture; and
sintering the shaped body.
15. A method for forming a ceramic component, comprising:
providing particles of a first ceramic material;
granulating particles of graphite and particles of a second ceramic material to form first granules containing graphite and the second ceramic material;
adding the particles of the first ceramic material and a fluid to the first granules, wherein adding the particles of the first ceramic material and the fluid is performed after granulating the particles of graphite and the particles of the second ceramic material;
mixing the first granules, the particles of the first ceramic material, and the fluid to form a mixture;
forming a shaped body from the mixture; and
sintering the shaped body.
16. The method of claim 15 , further comprising:
mixing the particles of graphite and the particles of the second ceramic material before granulating the particles of graphite and the particles of the second ceramic material; and
granulating the first granules and the particles of the first ceramic material to form second granules containing graphite, the first ceramic material, and the second ceramic material, wherein the second granules are formed after mixing the first granules, the particles of the first ceramic material, and the fluid,
wherein forming the shaped body is performed such that the shaped body includes the second granules.
17. The method of claim 15 , wherein granulating the particles of graphite and the particles of the first ceramic material is carried out by spray drying or casting.