Acetoacetylated polyvinyl polymers and curable coating compositions made therefrom
View Patent ↗The present invention relates to curable coating compositions containing acetoacetylated polyvinyl polymers obtained from polyvinyl polymers, such as polyvinyl butyrals. These coating compositions are especially suitable for use as wash primers in automotive OEM and refinish coating applications.
1. A curable coating composition comprising crosslinkable and crosslinking components wherein said crosslinkable component comprises:
(a) an acetoacetylated polyvinyl polymer having the formula:
wherein (m) ranges from about 1.5 mole percent to about 85 mole percent, (n) ranges from about 0 mole percent to about 20.5 mole percent, (p) ranges from about 12 mole percent to about 87 mole percent and (q) ranges from about 1 mole percent to about 88 mole percent, sum of (m), (n), (p) and (q) being 100 and wherein R 1 and R 2 are independently H, substituted or unsubstituted C 1 to C 12 alkyl, substituted or unsubstituted C 6 to C 14 aryl, substituted or unsubstituted C 7 to C 22 aralkyl, substituted or unsubstituted C 6 to C 14 alkaryl, substituted, unsubstituted C 4 to C 14 carbocyclyl or a combination thereof, said substituents being independently selected from the group consisting of C 1 to C 12 alkoxy, acyl, carboxyl, derivative of carboxyl, sulfonyl, derivative of sulfonyl, cyano, and halo;
(b) an acetoacetylated polyvinyl polymer having the formula:
wherein (m) ranges from about 1.5 mole percent to about 85 mole percent, (n) ranges from about 0 mole percent to about 20.5 mole percent, (p) ranges from about 12 mole percent to about 87 mole percent, (q) ranges from about 1 mole percent to about 88 mole percent and (x) ranges from about 0.5 to about 6 mole percent, sum of (m), (n), (p), (q) and (x) being 100 and wherein R 1 and R 2 are independently H, substituted or unsubstituted C 1 to C 12 alkyl, substituted or unsubstituted C 6 to C 14 aryl, substituted or unsubstituted C 7 to C 22 aralkyl, substituted or unsubstituted C 6 to C 14 alkaryl, substituted, unsubstituted C 4 to C 14 carbocyclyl or a combination thereof, and wherein Z is H, or —COOH and Y is —COOH, halo, unsubstituted phenyl or a combination thereof; said substituents being independently selected from the group consisting of C 1 to C 12 alkoxy, acyl, carboxyl, derivative of carboxyl, sulfonyl, derivative of sulfonyl, cyano, and halo; or
(c) a combination thereof; and
wherein said crosslinking component comprises a polyamine, a polyketimine, polyepoxide, polyisocyanate, melamine, C 1 to C 12 alkyl dialdehyde, C 1 to C 12 alkyl poly(meth)acrylate, or a combination thereof.
2. The coating composition of claim 1 wherein in said acetoacetylated polyvinyl polymer R 1 is propyl and R 2 is methyl.
3. The coating composition of claim 1 wherein GPC weight average molecular weight of said acetoacetylated polyvinyl polymer ranges from about 20,000 to about 300,000.
4. The coating composition of claim 1 wherein Tg of the acetoacetylated polyvinyl polymer ranges from about 40° C. to about 60° C.
5. The coating composition of claim 1 wherein said acetoacetylated polyvinyl polymer is solubilized in one or more solvents.
6. The coating composition of claim 1 wherein said crosslinking component comprises a polyamine, a polyketimine, or a combination thereof.
7. The coating composition of claim 1 wherein VOC of said composition ranges from 0.1 to 0.72 kilograms per liter of said composition.
8. The curable coating composition of claim 1 wherein said acetoacetylated polyvinyl polymer is produced by the steps comprising:
(i) dissolving in one or more solvents:
(a) a polyvinyl polymer having the formula:
wherein (m) ranges from about 1.5 mole percent to about 85 mole percent, (n) ranges from about 0 mole percent to about 20.5 mole percent and (o) ranges from about 13 mole percent to about 98.5 mole percent, sum of (m), (n) and (o) being 100 and wherein R 1 and R 2 are independently H, substituted or unsubstituted C 1 to C 12 alkyl, substituted or unsubstituted C 6 to C 14 aryl, substituted or unsubstituted C 7 to C 22 aralkyl, substituted or unsubstituted C 6 to C 14 alkaryl, substituted, unsubstituted C 4 to C 14 carbocyclyl or a combination thereof, said substituents being independently selected from the group consisting of C 1 to C 12 alkoxy, acyl, carboxyl, derivative of carboxyl, sulfonyl, derivative of sulfonyl, cyano, and halo;
(b) a polyvinyl polymer having the formula:
wherein (m) ranges from about 1.5 mole percent to about 85 mole percent, (n) ranges from about 0 mole percent to about 20.5 mole percent and (o) ranges from about 13 mole percent to about 98.5 mole percent and (x) ranges from about 0.5 to about 6 mole percent, sum of (m), (n), (o) and (x) being 100 and wherein R 1 and R 2 are independently H, substituted or unsubstituted C 1 to C 12 alkyl, substituted or unsubstituted C 6 to C 14 aryl, substituted or unsubstituted C 7 to C 22 aralkyl, substituted or unsubstituted C 6 to C 14 alkaryl, substituted, unsubstituted C 4 to C 14 carbocyclyl or a combination thereof, and wherein Z is H, or —COOH and Y is —COOH, halo, unsubstituted phenyl or a combination thereof; said substituents being independently selected from the group consisting of C 1 to C 12 alkoxy, acyl, carboxyl, derivative of carboxyl, sulfonyl, derivative of sulfonyl, cyano, and halo; or
(c) a combination of thereof to form a solution;
(ii) contacting said solution with C 1 to C 12 alkyl acetoacetate to produce said acetoacetylated polyvinyl polymer.
9. The composition of claim 8 wherein said R 1 is propyl and said R 2 is methyl.
10. The coating composition of claim 1 formulated as automotive refinish or OEM wash primer composition.