Positive electrode active material, non-aqueous electrolyte secondary battery containing the same and method for evaluating positive electrode active material
View Patent ↗A positive electrode active material powder for a non-aqueous electrolyte secondary battery, wherein an amount of a liquid reagent absorbed by the powder is 20 to 40 ml per 100 g of the powder when the liquid reagent is dibutyl phthalate, and the amount is 20 to 50 ml per 100 g of the powder when the liquid reagent is N-methyl-2-pyrrolidone or water, the absorption amount is a value measured using a device according to test method A or B regarding DBP absorption based on JIS K6217 (1997), and the measured value is an amount of the liquid reagent added until the viscosity of a mixture of the powder and the liquid reagent reaches a level corresponding to 70% of a maximum torque which is recorded when a change in the viscosity of a mixture of the powder and the liquid reagent is measured by a torque detecting device.
1. A positive electrode active material for a non-aqueous electrolyte secondary battery comprising a lithium-containing composite oxide powder, wherein an absorption amount of a liquid reagent absorbed by said powder is 20 to 40 ml per 100 g of said powder when said liquid reagent is dibutyl phthalate (DBP), and an absorption amount of a liquid reagent absorbed by said powder is 20 to 50 ml per 100 g of said powder when said liquid reagent is N-methyl-2-pyrrolidone (NMP) or water,
said absorption amount is a value measured using a device according to A test method or B test method regarding DBP absorption based on JIS K6217 (1997),
said measured value is an amount of said liquid reagent added until the viscosity of a mixture of said powder and said liquid reagent reaches a level corresponding to 70% of maximum torque which is recorded when said powder is introduced into said device, and said liquid reagent is added dropwise thereto, during which a change in the viscosity of a mixture of said powder and said liquid reagent is measured by a torque detecting device, and
wherein, said lithium-containing composite oxide powder is represented by a formula Li a MO 2 , where M is selected from the group consisting of Co, CoMg, CoAl, CoMn and CoNi.
2. A non-aqueous electrolyte secondary battery comprising:
an electrode group comprising a negative electrode plate, a positive electrode plate containing the positive electrode active material according to claim 1 , and a separator interposed between said negative electrode plate and said positive electrode plate;
a battery case for housing said electrode group; and
a non-aqueous electrolyte to be injected into said battery case.