Coated article with high visible transmission and low emissivity
View Patent ↗A coated article that can be used in applications such as insulating glass (IG) units, so that resulting IG units can achieve high visible transmission of at least 70% (e.g., when using clear glass substrates from 1.0 to 3.5 mm thick), combined with at least one of: (a) SHGC no greater than about 0.45, more preferably no greater than about 0.40; (b) SC no greater than about 0.49, more preferably no greater than about 0.46; (c) chemical and/or mechanical durability; (d) neutral transmissive color such that transmissive a* is from −5.0 to 0 (more preferably from −3.5 to −1.5), and transmissive b* is from −2.0 to 4.0 (more preferably from 1.0 to 3.0); and (e) neutral reflective color from the exterior of the IG unit (i.e., Rg/R out ) such that reflective a* is from −3.0 to 2.0 (more preferably from −2.0 to 0.5), and reflective b* is from −5.0 to 1.0 (more preferably from −4.0 to −1.0). In certain example non-limiting embodiments, coated articles herein comprise: substrate/TiO x /ZnO x /Ag/NiCrO x /SnO x /ZnO x /Ag/NiCrO x /SnO x /Si x N y .
1. A method of making a coated article including a coating supported by a glass substrate, the method comprising:
providing a glass substrate;
sputtering a coating on the glass substrate, the coating comprising at least the following layers on the glass substrate:
a layer comprising zinc oxide;
a layer comprising silver over and contacting the layer comprising zinc oxide; and
a layer comprising nickel chromium oxide over and contacting the layer comprising silver, wherein the layer comprising nickel chromium oxide is sputter-deposited in an atmosphere comprising oxygen gas so as to be oxidized throughout its thickness as deposited;
a dielectric layer provided over at least the layer comprising nickel chromium oxide;
another layer comprising zinc oxide;
another layer comprising silver located over and contacting the another layer comprising zinc oxide;
wherein there are no more than two layers comprising silver in the coating; and
at least one dielectric layer provided over the another layer comprising silver; and
wherein the coating has a sheet resistance (R s ) of no greater than 5.0 ohms/square, and the coated article has a visible transmission of at least 70%.
2. The method of claim 1 , further comprising coupling the glass substrate with the coating thereon to another substrate in making an insulating glass (IG) window unit.
3. The method of claim 1 , wherein the coating has a sheet resistance (R s ) of no greater than 3.5 ohms/square.
4. The method of claim 1 , wherein the coating has a sheet resistance (R s ) of no greater than 2.8 ohms/square.
5. The method of claim 1 , wherein the coated article has an SHGC of no greater than 0.45.
6. The method of claim 1 , wherein the coated article has an a* glass side reflectance (a* g ) of from 0 to 2.5.
7. The method of claim 1 , wherein the coated article has a b* glass side reflectance (b* g ) of from −5.0 to 0.
8. The method of claim 1 , wherein an uppermost layer of the coating comprises carbon or silicon nitride.