High strength seamless steel pipe excellent in hydrogen-induced cracking resistance
View Patent ↗A high strength seamless steel pipe having mgh yield stress and excellent hydrogen-induced cracking resistance, comprises by mass %, C: 0.03 - 0.11 %, Si: 0.05 - 0.5 %, Mn: 0.8 - 1.6 %, p: 0.025 % or less, S: 0.003 % or less, Ti: 0.002 - 0.017 %, Al: 0.001 - 0.10 %, Cr: 0.05 - 0.5 %, Mo: 0.02 - 0.3 %, V: 0.02 - 0.20 %, Ca 0.0005 - 0.005 %, N: 0.008 % or less and O (Oxygen): 0.004 % or less, the balance Fe and impurities. The steel microstructure is bainite and/or martensite and ferrite is precipitated at grain boundaries. The seamless steel pipe can contain at least one of Cu: 0.05 - 0.5 % and Ni: 0.05 - 0.5 %. To produce the pipe, it is desirable to limit a starting temperature of quenching after rolling, a cooling rate and a tempering temperature.
1. A high strength seamless steel pipe excellent in hydrogen-induced cracking resistance, characterized by consisting essentially of, by mass %, C: 0.03-0.11%, Si: 0.05-0.5%, Mn: 0.8-1.6%, P: 0.025% or less, S: 0.003% or less, Ti: 0.002-0.017%, Al: 0.001-0.10%, Cr: 0.05-0.5%, Mo: 0.02-0.3V: 0.02-0.20%, Ca: 0.0005-0.005%, N: 0.008% or less and O (Oxygen): 0.004% or less, and the balance Fe and impurities, and also characterized in that the microstructure of the steel is bainite and martensite, ferrite is precipitated at grain boundaries and yield stress is 483 MPa or more.
2. A high strength seamless steel pipe excellent in hydrogen-induced cracking resistance according to claim 1 , characterized by further containing, by mass %, at least one of Cu: 0.05-0.5% and Ni: 0.05-0.5%.