Magnetic recording medium having narrow pulse width characteristics
View Patent ↗A dual-layer magnetic recording medium including a non-magnetic substrate having a front side and a back side, a lower support layer formed over the front side and a magnetic upper recording layer formed over the lower layer, wherein the magnetic layer contains a volume concentration of at least about 35% of a magnetic metallic particulate pigment having a coercivity of at least about 2000 Oersteds (Oe), and a binder system for the pigment. The magnetic recording medium exhibits an orientation ratio greater than 2.0, a pulsewidth (PW50) value of less than about 500 nm, and a remanence-thickness product, Mr*t, of less than about 5.0 memu/cm 2 .
1. A dual-layer magnetic recording medium comprising a non-magnetic substrate having a front side and a back side, a lower support layer formed over the front side and a magnetic upper recording layer formed over said lower support layer, the magnetic upper recording layer comprising a volume concentration of at least about 35% of a primary magnetic metallic particulate pigment having a coercivity of at least about 2300 Oe, the magnetic pigment particles having an average particle length of no more than about 80 nm and a binder for the pigment, wherein said medium has a remanence-thickness product Mr*t, of less than or equal to about 2.84 memu/cm 2 , an orientation ratio greater than about 2.0, and a PW50 of less than or equal to about 384 nm.
2. The medium of claim 1 , wherein the coercivity is at least about 2500 Oe.
3. The medium of claim 1 , having an orientadon ratio greater than about 2.2.
4. The medium of claim 1 , wherein said upper magnetic layer comprises said magnetic metallic particulate pigment in a volume concentration of at least about 40%.
5. The medium of claim 1 , wherein said magnetic recording layer further comprises a large carbon particle material having a particle size of from about 50 to about 500nm.
6. The medium of claim 1 , wherein the upper recording layer comprises a primary ferromagnetic pigment, aluminum oxide, a spherical large particle carbon material having a particle size of from about 50 to about 500 nm, a polyurethane binder, a vinyl chloride binder, a hardener, a fatty acid ester lubricant, and a fatty acid lubricant.
7. The medium of claim 1 , wherein said lower support layer comprises:
a pigment powder that is essentially nonmagnetic or a soft magnetic powder having a coercivity of less than about 300 Oe, and a resin binder system therefor.
8. The medium of claim 7 , wherein said lower support layer further includes a fatty acid ester lubricant, a faty acid lubricant dispersed in said binder.
9. The medium of claim 1 , wherein said binder comprises a hard resin component and a soft resin component.
10. The medium of claim 9 , wherein said soft resin component is a polyurethane resin.
11. The medium of claim 9 , wherein said hard resin component is a vinyl chloride resin.
12. The medium of claim 9 , wherein said hard resin component is a nonhalogenated vinyl resin.
13. The medium of claim 1 , further comprising a back coat coated on said back side of said substrate.
14. The medium of claim 13 , wherein the back coat includes a carbon black pigment a urethane binder, and at least one compound selected from phenoxy resin and nitrocellulose.
15. The medium of claim 13 , wherein the back coat comprises a carbon black pigment and a metal oxide selected from titanium dioxide, aluminum oxide, and a mixture thereof.
16. A dual-layer magnetic recording medium comprising a non-magnetic substrate having a front side and a back side, a lower support layer formed over the front side and a magnetic upper recording layer formed over said lower support layer, the magnetic upper recording layer comprising a volume concentration of at least about 35% of a primary magnetic metallic particulate pigment having a coercivity of at least about 2500 Oe, the magnetic pigment particles having an average particle length of no more than about 80 nm, and a binder for the pigment wherein said medium has a remanence-thickness product Mr*t, of less than or equal to about 2.12 memu/cm 2 , an orientation ratio greater than about 2.0, and a PW50 of less than or equal to about 366 nm.
17. The medium of claim 16 , wherein the remanence-thickness product Mr*t, is less than or equal to about 1.59 memu/cm 2 , and the PW50 is less than or equal to about 361 nm.
18. The medium of claim 17 , wherein the coercivity is at least about 2640 Oe, the remanence-thickness product, Mr*t, is less than or equal to about 1.14 memu/cm 2 , and the PW50 is less than or equal to about 343 nm.