Co-extruded generating bank swaged tubing
View Patent ↗A method is provided for successfully rolling co-extruded tubing into drums of a boiler bank. First, a co-extruded tube is provided, containing a carbon steel base tubing with an outer layer of high alloy tubing. Next, the outer layer of high alloy tubing is removed by machining in the area of the co-extruded tubing that is to be rolled into the drum. Then, the co-extruded tubing is swaged using multiple swaging steps and annealing treatments. The co-extruded tubing is swaged to the required diameter and wall thickness. Finally, co-extruded tubing is inserted, rolled, and sealed into the drums.
1. A method for successfully rolling co-extruded tubing into drums of a boiler bank in a corrosion and erosion boiler environment comprising the steps of:
providing a co-extruded tubing containing a carbon steel base tubing, an outer layer of high alloy tubing, an area that is to be rolled into the drum by machining, and an area that is to be exposed to the boiler environment;
removing the outer layer of high alloy tubing in the area that is to be rolled into the drum by machining;
swaging the co-extruded tubing using multiple swaging steps and annealing treatments to swage the co-extruded tubing to a required diameter and wall thickness;
inserting the co-extruded tubing into the drums;
rolling the co-extruded tubing; and
sealing the co-extruded tubing into the drums.
2. A method according to claim 1 , wherein said high alloy tubing comprises a Nickel-Iron-Chromium alloy with additions of Molybdenum and Copper.
3. A method according to claim 1 ,wherein said high alloy tubing comprises stainless steel.
4. A method according to claim 1 , wherein the outer layer of high alloy tubing is removed with a tapered machine.
5. A method according to claim 1 , wherein the outer layer of high alloy tubing is swaged into the surface of the carbon steel inner base tubing.
6. A method according to claim 1 , including the step of utilizing a cutting tool mounted on a lathe to remove the outer layer of high alloy tubing in the area that is to be rolled into the drum by machining.